Abstract
Dendritic core–shell architectures containing poly (glycerol) and poly (ethylene imine) cores and poly(lactide) shell (PG-PLA and PEI-PLA respectively) were synthesized. Analogous of these core–shell architectures containing the same cores but poly (L-lactide) shell (PG-PLLA and PEI-PLLA, respectively) were also synthesized. In this work PG and PEI were used as macroinitiator for ring opening polymerization of the lactid and L-lactide monomers. Different molar ratios of monomer to end functional groups of PG ([LA]/[OH]) and PEI ([LA]/[NHn] (n = 1 or 2)) were used to prepare the core–shell architectures with different shell thickness. These core–shell architectures were able to encapsulate and transport the small guest molecules. Their transport capacity (TC) depended on the type and thickness of the shells. TC of core–shell architectures containing PLLA shell was higher than that for their analogs containing PLA shell. The diameter of core–shell architectures was between 20–80 nm. The rate of release of guest molecules from chloroform solution of nanocarriers to water phase was investigated and it depended on the type of the core, shell and solvent.
Similar content being viewed by others
References
Adeli M. & R. Hagg, 2006. Multiarm star nanocarriers containing a poly(ethylene imine) core and polylactide arms J. Polym. Sci. Part A: Polym, Chem. 44, 5740–5749
Astruc D., Chardac F. 2001 Chem Rev 101:2991
Daniel M.-C., Astruc D. 2004 Chem Rev 104:293
Frey H. & R. Haag, 2001. Hyperbranched polymers in industry In: Cahn R.H., Buschow K.H.J., Flemings M.C., Ilschner B., Kramer E.J. and Majahan. S. eds. Encyclopedia of Materials: Science and Technology. Elsevier Science Ltd, Oxford, pp. 3997–4000.
Frey H., Haag R. 2002 Rev. Mol. Biotechnol. 90:257
Haag R. 2004a Angew Chem 116:280
Haag R. 2004b Angew Chem Int Ed 43:278
Haag R., Krämer M., Stumbé J.-F., Kautz H. 2001 Poly. Mat. Sci. Eng. 84:69
Haag R., Krämer M., Stumbé J.-F., Krause S., Komp A., Prokhorova S. 2002a Polymer Preprints 43:328
Haag R., H. Türk & S. Meeling, 2002b. DE10211664A1.
Haag R., Stumbe´ J.-F., Sunder A., Frey H., Hebel A. 2000a Macromolecules 33:8158
Haag R., Sunder A., Stumbé J.-F. 2000b J. Am. Chem. Soc. 122:2954
Krämer M., Stumbé J.-F., Grimm G., Kaufmann B., Ute Krüger U., Weber M., Haag R. 2004 ChemBioChem 5:1081
Krämer M., Stumbé J.-F., Türk H., Krause S., Komp A., Delineau L., Prokhorova S., Kautz H., Haag R. 2002a Angew. Chem. Int. Ed. 41:4252
Krämer M., Stumbé J.-F., Türk H., Krause S., Komp A., Delineau L., Prokhorova S., Kautz H., Haag R. 2002b Angew. Chem. 114:4426
Roark D.N., B.C. McKusick & U. Steuerle, 2000. In: Ullmanns Encyclopedia of Industrial Chemistry, 6th edn. Electronic Release, Aziridines.
Scherr G., U. Steuerle & R. Fikentscher, 1997. In: Kirk-Othmer. Imines, cyclic. 4th edn., Vol. 14, pp.2–40.
Steuerle U., W. Reuther & W. Harder, 1997. BASF AG, WO 97/21760.
Stiriba S.-E., Frey H., Haag R. 2002a Angew. Chem. 114:1385
Stiriba S.-E., Frey H., Haag R. 2002b Angew. Chem. Int. Ed. 41:1329
Stiriba S.-E., Kautz H., Frey H. 2002c J. Am. Chem. Soc. 124:9698
Sunder A., Krämer M., Hanselmann R., Mülhaupt R., Frey H. 1999a Angew. Chem. 111:3758
Sunder A., Krämer M., Hanselmann R., Mülhaupt R., Frey H. 1999b Angew. Chem. Int. Ed. 38:3552
Sunder A., Mülhaupt R., Haag R., Frey H. 2000a Macromolecules 33:253
Sunder A., Türk H., Haag R., Frey H. 2000b Macromolecules 33:7682
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Adeli, M., Haag, R. & Zarnegar, Z. Effect of the shell on the transport properties of poly(glycerol) and Poly(ethylene imine) nanoparticles. J Nanopart Res 9, 1057–1065 (2007). https://doi.org/10.1007/s11051-006-9188-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11051-006-9188-0