Abstract
To study the damage evolution behavior of polypropylene fiber reinforced concrete (PFRC) subjected to sulfate attack, a uniaxial compression test was carried out based on acoustic emission (AE). The effect of sulfate attack relative to time and fiber hybridization were analyzed and the compression damage factor was calculated using a mathematical model. The changes to AE ringing counts during the compression could be divided into compaction, elastic, and AE signal hyperactivity stages. In the initial stage of sulfate attack, the concrete micropores and microcracks were compacted gradually under external load and a corrosion products filling effect, and this corresponded with detection of few AE signals and with concrete compression strength enhancement. With increasing sulfate attack time, AE activity decreased. The cumulative AE ringing counts of PFRC at all corrosion ages were much higher than those for plain concrete. PFRC could still produce AE signals after peak load due to drawing effect of polypropylene fiber. After 150 d of sulfate attack, the cumulative AE ringing counts of plain concrete went down by about an order of magnitude, while that for PFRC remained at a high level. The initial damage factor of hybrid PFRC was −0.042 and −0.056 respectively after 150 d of corrosion, indicating that the advantage of hybrid polypropylene fiber was more obvious than plain concrete and single-doped PFRC. Based on a deterioration equation, the corrosion resistance coefficient of hybrid PFRC would be less than 0.75 after 42 drying-wetting sulfate attack cycles, which was 40% longer than that of plain concrete.
Similar content being viewed by others
References
Liu Y M, Yu H M, Wang C, Wang C L. Research on mechanism of damage of anhydrock in dolomite layer to tunnel structure. Rock and Soil Mechanics, 2011, 32(9): 2704–2708
Xing Z S, Deng M, Wang A G, Liu K W. Internal sulfate attack on concrete caused by gypsum-bearing aggregates. Journal of Building Materials, 2014, 17(1): 30–34
Raphael I T, Barzin M. Modeling of damage in cement-based materials subjected to external sulfate attack. II: Comparison with experiments. Journal of Materials in Civil Engineering, 2003, 15(4): 314–322
Zuo X B, Sun W. Full process analysis of damage and failure of concrete subjected to external sulfate attack. Journal of the Chinese Ceramic Society, 2009, 37(07): 1063–1067
Meng K, Xu L H, Chi Y. Experimental investigation on the mechanical behavior of hybrid steel-polypropylene fiber reinforced concrete under conventional triaxial cyclic compression. Construction & Building Materials, 2021, 291: 123262
Holovata Z, Kirichenko D, Korneeva I, Neutov S, Vyhnanets M. Experimental studies of fiber-reinforced concrete under axial tension. Materials Science Forum, 2021, 6266: 323–329
Hugo C, João P C R, Pimienta P. Flexural strength at high temperatures of a high strength steel and polypropylene fiber concrete. Construction & Building Materials, 2019, 227: 116721
Yang J, Chen B C, Nuti C. Influence of steel fiber on compressive properties of ultra-high performance fiber-reinforced concrete. Construction & Building Materials, 2021, 302: 124104
Qin Y, Duan M H, Ma W L, Li Y L, Zhou H. Experimental study on the damage permeability of polypropylene fiber-reinforced concrete. Construction & Building Materials, 2021, 286: 122592
Wang J H. The study of steel fiber reinforced concrete durability based on damage mechanics. Research Journal of Applied Sciences, Engineering and Technology, 2014, 7(3): 543–550
Liang N H, Liu X R, Sun J. Uniaxial tensile test of multi-scale polypropylene fiber reinforced concrete. Journal of Chongqing University, 2012, 35(6): 80–84
Liu X R, Ke W, Liang N H, Miao Q X, Yang P. Study on the dynamic mech anical properties of concrete multi size polypropylene fiber based on SHPB test. Materials Reports, 2018, 32(S1): 484–489
Liang N H, Liu X R, Sun J. Experimental study of crack resistance for multi-scale polypropylene fiber reinforced concrete. Journal of China Coal Society, 2012, 37(8): 1304–1309
Liang N H, Dai J F, Liu X R, Zhong Z L. Experimental study on the fracture toughness of concrete reinforced with multi-size polypropylene fiber concrete. Thesis for the Master’s Degree. Chongqing: Chongqing University, 2018
Geng J S, Sun Q, Zhang Y C, Cao L W, Zhang W Q. Studying the dynamic damage failure of concrete based on acoustic emission. Construction & Building Materials, 2017, 149: 9–16
Rabczuk T, Belytschko T. Cracking particles: A simplified meshfree method for arbitrary evolving cracks. International Journal for Numerical Methods in Engineering, 2004, 61(13): 2316–2343
Rabczuk T, Belytschko T. A three-dimensional large deformation meshfree method for arbitrary evolving cracks. Computer Methods in Applied Mechanics and Engineering, 2007, 196(29–30): 2777–2799
Rabczuk T, Zi G, Bordas S, Nguyen-Xuan H. A simple and robust three-dimensional cracking-particle method without enrichment. Computer Methods in Applied Mechanics and Engineering, 2010, 199(37–40): 2437–2455
Ren H L, Zhuang X Y, Anitescu C, Rabczuk T. An explicit phase field method for brittle dynamic fracture. Computers & Structures, 2019, 217: 45–56
Ren H L, Zhuang X Y, Rabczuk T. A higher order nonlocal operator method for solving partial differential equations. Computer Methods in Applied Mechanics and Engineering, 2020, 367: 113132
Trąmpczyński W, Goszczyńska B, Bacharz M. Acoustic emission for determining early age concrete damage as an important indicator of concrete quality/condition before loading. Materials (Basel), 2020, 13(16): E3523
Jiao Y B, Zhang Y, Guo M, Zhang L D, Ning H, Liu S Q. Mechanical and fracture properties of ultra-high performance concrete (UHPC) containing waste glass sand as partial replacement material. Journal of Cleaner Production, 2020, 277: 123501
Tetsuya S, Saki N, Yuma S, Tomoki S, Masayasu O. Damage estimation of concrete canal due to freeze and thawed effects by acoustic emission and X-ray CT methods. Construction & Building Materials, 2020, 245: 118343
Tetsuya S, Masayasu O, Mitsuhiro S. Relative damage evaluation of concrete in a road bridge by AE rate-process analysis. Materials and Structures, 2007, 40(2): 221–227
Wang Y, Chen S J, Ge L, Zhou L, Hu H X. Analysis of dynamic tensile process of fiber reinforced concrete by acoustic emission technique. Journal of Wuhan University of Technology-Materials Science Edition, 2018, 33(5): 1129–1139
Alireza F, Anastasios C M, Theodore E M, Hamidreza F, Dimitrios G A. Fracture mode identification in cementitious materials using supervised pattern recognition of acoustic emission features. Construction & Building Materials, 2014, 67: 129–138
Yuma K, Tomoyo W, Tomoe K, Masayasu O. Corrosion mechanisms in reinforced concrete by acoustic emission. Construction & Building Materials, 2013, 48: 1240–1247
Qi F, Yang B, Li X B. Research on damage evolution of polypropylene fiber concrete under splitting load. Advances in Building Materials, 2011, 1278: 287–291
Xu L H, Wei C M, Li B. Damage evolution of steel-polypropylene hybrid fiber reinforced concrete: Experimental and numerical investigation. Advances in Materials Science and Engineering, 2018, 2018: 1719427
Yang X, Liang N H, Liu X R, Zhong Z L. A study of test and statistical damage constitutive model of multi-size polypropylene fiber concrete under impact load. International Journal of Damage Mechanics, 2019, 28(7): 973–989
Hamdia K M, Silani M, Zhuang X Y, He P F, Rabczuk T. Stochastic analysis of the fracture toughness of polymeric nanoparticle composites using polynomial chaos expansions. International Journal of Fracture, 2017, 206(2): 215–227
Alireza F, Salamone S, Bismarck L, Andrew W. Acoustic emission monitoring of a reinforced concrete shear wall by b-value-based outlier analysis. Structural Health Monitoring—An International Journal, 2013, 12(1): 3–13
Zhang J, Han Y D, Gao Y. Effects of water-binder ratio and coarse aggregate content on interior humidity, autogenous shrinkage, and drying shrinkage of concrete. Journal of Materials in Civil Engineering, 2014, 26(1): 184–189
Hong J Y, Jae H K, Hyo-Gyoung K. Experimental simulation of bleeding under a high concrete column. Cement and Concrete Research, 2014, 57: 61–69
Chen Y L, Shao W, Zhou Y C. Elastoplastic damage constitutive model of water-saturated concrete under uniaxial compression. Engineering Mechanics, 2011, 28(11): 59–63
Yan Y D, Jin W L, Wang H L, Lu C H. Chloride transport in cracked concrete under wet-dry cycling condition. Journal of Central South University, 2013, 44(5): 2060–2067 (in Chinese)
Yin G J, Zuo X B, Tang Y J, Olawale A, Wang J L. Numerical simulation on time-dependent mechanical behavior of concrete under coupled axial loading and sulfate attack. Ocean Engineering, 2017, 142: 115–124
Vrijdaghs R, Di Prisco M, Vandewalle L. Short-term and creep pull-out behavior of polypropylene macrofibers at varying embedded lengths and angles from a concrete matrix. Construction & Building Materials, 2017, 147: 858–864
Liu B X, Huang J L, Wang Z Y, Liu L. Study on damage evolution and acoustic emission character of coal-rock under uniaxial compression. Chinese Journal of Rock Mechanics and Engineering, 2009, 28(S1): 3234–3238
Li X P, Lu Y N, Wang Y J. Research on damage model of single jointed rock masses under coupling action of freeze-thaw and loading. Chinese Journal of Rock Mechanics and Engineering, 2013, 32(11): 2307–2315
Wang H Y, Qiu W G, Du L F, Gong L. Durability prediction model for tunnel lining concrete under sulfate corrosion. Modern Tunnelling Technology, 2014, 51(3): 91–97
Ministry of Housing and Urban-Rural Development of the People’s Republic of China. Standard for Design of Concrete Structure Durability, GB/T 50476-2019. Beijing: China Architecture and Building Press, 2019 (in Chinese)
Acknowledgements
The support from Mechanical Effect and Safety Analysis of Severely Damaged Tunnel Renovation Process (No. H20210058) is gratefully acknowledged. The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Liang, N., Mao, J., Yan, R. et al. The damage evolution behavior of polypropylene fiber reinforced concrete subjected to sulfate attack based on acoustic emission. Front. Struct. Civ. Eng. 16, 316–328 (2022). https://doi.org/10.1007/s11709-022-0810-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11709-022-0810-8