Corrosion performance of chemically synthesized poly(aniline-co-o-toluidine) copolymer coating on mild steel

  • Published:
Journal of Coatings Technology and Research Aims and scope Submit manuscript

Abstract

A soluble copolymer from aniline and o-toluidine [poly(aniline-co-o-toluidine)] was synthesized by chemical oxidative copolymerization using ammonium persulphate as an oxidant in hydrochloride aqueous medium. The resultant copolymer was characterized by Fourier Transform Infrared (FTIR) spectroscopy and chemically deposited on mild steel specimens using N-methyl-2-pyrrolidone (NMP) as solvent via solution evaporation method. The anticorrosive properties of copolymer coating was investigated in major corrosive environments, such as 0.1 M HCl, 5% NaCl solution, artificial seawater, distilled water and open atmosphere by conducting various corrosion tests which include: immersion test, open circuit potential (OCP) measurements, potentiodynamic polarization measurements and atmospheric exposure test. The corrosion performance of copolymer coating was also compared separately with polyaniline (PANi) and poly(o-toluidine) (POT) homopolymer coatings. The surface morphologies of polymer coatings were evaluated using scanning electron microscopy (SEM). The synthesized copolymer exhibited excellent protection against mild steel corrosion; the protection efficiency being in the range of 78–94% after 30 days of immersion. The corrosion performance of copolymer in 5% NaCl and artificial seawater was comparable, which was only marginally better than in 0.1 M HCl. In general, the performance of copolymer coating was found to be better than that of homopolymer coatings.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

Similar content being viewed by others

References

  1. Lu, WK, Basak, S, Elsenbaumer, RL, “Corrosion Inhibition of Metals by Conductive Polymer.” In: Skotheim, TA, Elsenbaumer, R, Reynolds, JR (eds.) Handbook of Conducting Polymers, pp. 881–920. M. Dekker (1998)

  2. Tan, CK, Blackwood, DJ, “Corrosion Protection by Multilayered Conducting Polymer Coatings.” Corros. Sci., 45 545–557 (2003)

    Article  CAS  Google Scholar 

  3. Borole, DD, Kapadi, UR, Mahulikar, PP, Hundiwale, DG, “Electrochemical Synthesis and Characterization of Conducting Copolymer: Poly(aniline-co-o-toluidine).” Mater. Lett., 60 2447–2452 (2006)

    Article  CAS  Google Scholar 

  4. Roy, BC, Gupta, MD, Ray, JK, “Studies on Conducting Polymers. 1. Aniline-Initiated Polymerization of Nitroanilines.” Macromolecules, 28 1727–1732 (1995)

    Article  CAS  Google Scholar 

  5. Ivanvo, S, Mokreva, P, Tsakova, V, Terlemezyan, L, “Electrochemical and Surface Structural Characterization of Chemically and Electrochemically Synthesized Polymer Layers—A Comparison.” Thin Solid Films, 441 44–49 (2003)

    Article  Google Scholar 

  6. Ahmad, N, MacDiarmid, AG, “Inhibition of Corrosion of Steels with the Exploitation of Conducting Polymer.” Synth. Met., 78 103–108 (1996)

    Article  CAS  Google Scholar 

  7. Kraljic, M, Mandic, Z, Duic, L, “Inhibition of Steel Corrosion by Polyaniline Coatings.” Corros. Sci., 45 181–198 (2003)

    Article  Google Scholar 

  8. Tallman, DE, Spinks, GM, Dominis, A, Wallace, GG, “Electro Active Conducting Polymers for Corrosion Control-Part-2 Ferrous Metals.” J. Solid State Electrochem., 6 85–100 (2002)

    Article  Google Scholar 

  9. Motheo, AJ, Pantoja, MF, Venancio, EC, “Effect of Monomer ratio in the Electrochemical Synthesis of Poly(aniline-co-o-methoxyaniline).” Solid. State. Ionics, 171 91–98 (2004)

    Article  CAS  Google Scholar 

  10. Hur, E, Berket, G, Sahin, Y, “Anti-Corrosive Properties of Polyaniline, Poly(2-toluidine) and Poly(aniline-co-2-toluidine) Coatings on Stainless Steel.” Curr. Appl. Phys., 7 597–604 (2007)

    Article  Google Scholar 

  11. Shinde, V, Sainkar, SR, Patil, PP, “Corrosion Protective Poly(o-toluidine) Coatings on Copper.” Corros. Sci., 47 1352–1369 (2005)

    Article  CAS  Google Scholar 

  12. Yalcinkaya, S, Tuken, T, Yazici, B, Ebril, M, “Electrochemical Synthesis and Corrosion Performance of Poly(pyrrole-co-o-anisidine).” Prog. Org. Coat., 62 236–244 (2008)

    Article  CAS  Google Scholar 

  13. Kuo, CT, Weng, SZ, Huang, RL, “Field-Effect Transistors of Polyaniline and Poly(2-alkylaniline) Thin Films as Semiconductor.” Synth. Met., 88 101–107 (1997)

    Article  CAS  Google Scholar 

  14. Wang, YZ, Joo, J, Hsu, CH, Pouget, JP, Epstein, AJ, “Charge Transport of Hydrochloric Acid Doped Polyaniline and Poly(o-toluidine) Fibers.” Macromolecules, 27 5826–5871 (1994)

    Google Scholar 

  15. Wei, Y, Focke, WW, Wnek, GE, Ray, A, Mac-Diarmid, AG, “Synthesis and Electrochemistry of Alkyl Ring-Substituted Polyanilines.” J. Phys. Chem., 93 495–499 (1989)

    Article  CAS  Google Scholar 

  16. Leclerc, M, Guay, J, Dao, LH, “Synthesis and Characterization of Poly(alkyl anilines).” Macromolecules, 22 649–653 (1989)

    Article  CAS  Google Scholar 

  17. Kumar, D, “Synthesis and Characterization of Poly(aniline-co-o-toluidine) Copolymer.” Synth. Met., 114 369–372 (2000)

    Article  CAS  Google Scholar 

  18. Li, XG, Huang, MR, Gu, GF, Qiu, W, Lu, JY, “Actual air Separation Through Poly(aniline-co-o-toluidine)/Ethyl Cellulose Blend Thin-Film Composite Membranes.” J. Appl. Polym. Sci., 75 458–463 (2000)

    Article  CAS  Google Scholar 

  19. Li, XG, Huang, MR, Yang, Y, “Synthesis and Characterization of Poly(aniline-co-xylidine)s.” Polym. J., 32 348–353 (2000)

    Article  CAS  Google Scholar 

  20. Huang, MR, Li, XG, Yang, YL, Wang, XS, Yan, D, “Oxidative Copolymers of Aniline with o-Toluidine: Their Structure and Thermal Properties.” J. Appl. Polym. Sci., 81 1838–1847 (2001)

    Article  CAS  Google Scholar 

  21. Vera, R, Schrebler, R, Cury, P, Del, RR, Romero, H, “Corrosion Protection of Carbon Steel and Copper by Polyaniline and Poly(o-methoxyaniline) Films in Sodium Chloride Medium: Electrochemical and Morphological Study.” J. Appl. Electrochem., 37 519–525 (2007)

    Article  CAS  Google Scholar 

  22. Ansari, R, Alikhani, AH, “Application of Polyaniline/Nylon Composites Coating for Corrosion Protection of Steel.” J. Coat. Technol. Res., 6 (2) 221–227 (2009)

    Article  CAS  Google Scholar 

  23. Ichinohe, D, Muranaka, T, Sasaki, T, Kobayashi, M, Kise, H, “Oxidative Polymerization of Phenylenediamines Catalyzed by Horseradish Peroxidise.” J. Polym. Sci, Part A: Polym. Chem., 36 2593–2600 (1998)

    Article  CAS  Google Scholar 

  24. Kang, ET, Neoh, KG, Tan, KL, “Polyaniline: A Polymer with Many Interesting Redox States.” Prog. Polym. Sci., 23 277–324 (1998)

    Article  CAS  Google Scholar 

  25. Schauer, T, Joos, A, Dulog, L, Eisenbach, CD, “Protection of Iron Against Corrosion with Polyaniline Primer.” Prog. Org. Coat., 33 20–27 (1998)

    Article  CAS  Google Scholar 

  26. Lu, WK, Elsenbaumer, RL, Wessling, B, “Corrosion Protection of Mild Steel by Coatings Containing Polyaniline.” Synth. Met., 71 2163–2166 (1995)

    Article  CAS  Google Scholar 

  27. Pud, AA, Shapoval, GS, Kamarchik, P, Ogurtsov, NA, Gromovaya, VF, Mayronyuk, IE, Konstur, YV, “Electrochemical Behaviour Of Mild Steel Coated by Polyaniline Doped with Organic Sulphonic Acids.” Synth. Met., 107 111–115 (1999)

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Corrosion Research Laboratory, Department of Applied Chemistry, Aligarh Muslim University, Aligarh, 202002, India

    M. Mobin & N. Tanveer

Authors
  1. M. Mobin
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. N. Tanveer
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to M. Mobin.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Mobin, M., Tanveer, N. Corrosion performance of chemically synthesized poly(aniline-co-o-toluidine) copolymer coating on mild steel. J Coat Technol Res 9, 27–38 (2012). https://doi.org/10.1007/s11998-011-9328-z

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11998-011-9328-z

Keywords

Search

Navigation