A Review on Silicide-Based Materials: Thermoelectric and Mechanical Properties

  • Published:
Metals and Materials International Aims and scope Submit manuscript

Abstract

Silicide-based thermoelectric (TE) materials are promising candidates for automotive TE generators, which can collect wasted heat and convert it into electricity. Adequate strategies should be used to manufacture highly efficient silicide-based TE devices. This review summarizes novel strategies for obtaining materials that feature excellent TE properties and mechanical reliability. Controlling the carrier concentration and band structure could increase their electronic transport properties, while nanostructure engineering could effectively reduce their lattice thermal conductivity. Moreover, well designed microstructures are required to obtain mechanically reliable TE materials, which indicates that precisely controlling their nanostructure is essential for the improved trade-off relationship between TE and mechanical properties. While many challenges should still be overcome, the development of highly efficient TE materials and devices could represent new solutions for the global energy crisis.

Graphic Abstract

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5

Reprinted with permission from [1]. Copyright 2019 J. Korean Ceram. Soc.)

Fig. 6
Fig. 7
Fig. 8
Fig. 9

Reprinted with permission from [5]. Copyright 2012 American Physical Society)

Fig. 10
Fig. 11
Fig. 12

Similar content being viewed by others

References

  1. G. Kim, W. Kim, W. Lee, J. Korean Ceram. Soc. 56, 435–442 (2019)

    CAS  Google Scholar 

  2. S.I. Kim, K.H. Lee, H.A. Mun, H.S. Kim, S.W. Hwang, J.W. Roh, D.J. Yang, W.H. Shin, X.S. Li, Y.H. Lee, G.J. Snyder, S.W. Kim, Science 348, 109–114 (2015)

    CAS  Google Scholar 

  3. W.-S. Liu, Q. Zhang, Y. Lan, S. Chen, X. Yan, Q. Zhang, H. Wang, D. Wang, G. Chen, Z. Ren, Adv. Energy Mater. 1, 577–587 (2011)

    CAS  Google Scholar 

  4. G. Kim, J. Kim, H. Lee, S. Cho, I. Lyo, S. Noh, B.-W. Kim, S.W. Kim, K.H. Lee, W. Lee, Scr. Mater. 116, 11–15 (2016)

    CAS  Google Scholar 

  5. W. Liu, X. Tan, K. Yin, H. Liu, X. Tang, J. Shi, Q. Zhang, C. Uher, Phys. Rev. Lett. 108, 166601 (2012)

    Google Scholar 

  6. H. Ning, G.D. Mastrorillo, S. Grasso, B. Du, T. Mori, C. Hu, Y. Xu, K. Simpson, G. Maizza, M.J. Reece, J. Mater. Chem. A 3, 17426–17432 (2015)

    CAS  Google Scholar 

  7. P. Gao, J.D. Davis, V.V. Poltavets, T.P. Hogan, J. Mater. Chem. C 4, 929–934 (2016)

    CAS  Google Scholar 

  8. Z. Li, J.-F. Dong, F.-H. Sun, S. Hirono, J.-F. Li, Chem. Mater. 29, 7378–7389 (2017)

    CAS  Google Scholar 

  9. A. Yamamoto, S. Ghodke, H. Miyazaki, M. Inukai, Y. Nishino, M. Matsunami, T. Takeuchi, Jpn. J. Appl. Phys. 55, 020301 (2016)

    Google Scholar 

  10. S. Chen, K.C. Lukas, W. Liu, C.P. Opeil, G. Chen, Z. Ren, Adv. Energy Mater. 3, 1210–1214 (2013)

    CAS  Google Scholar 

  11. W. Zhao, Z. Liu, Z. Sun, Q. Zhang, P. Wei, X. Mu, H. Zhou, C. Li, S. Ma, D. He, P. Ji, W. Zhu, X. Nie, X. Su, X. Tang, B. Shen, X. Dong, J. Yang, Y. Liu, J. Shi, Nature 549, 247–251 (2017)

    CAS  Google Scholar 

  12. G. Rogl, A. Grytsiv, P. Rogl, N. Peranio, E. Bauer, M. Zehetbauer, O. Eibl, Acta Mater. 63, 30–43 (2014)

    CAS  Google Scholar 

  13. M.S. Kim, W.J. Lee, K.H. Cho, J.P. Ahn, Y.M. Sung, ACS Nano 10, 7197–7207 (2016)

    CAS  Google Scholar 

  14. Y. Pei, G. Tan, D. Feng, L. Zheng, Q. Tan, X. Xie, S. Gong, Y. Chen, J.-F. Li, J. He, M.G. Kanatzidis, L.-D. Zhao, Adv. Energy Mater. 7, 1601450 (2017)

    Google Scholar 

  15. K. Biswas, J. He, Q. Zhang, G. Wang, C. Uher, V.P. Dravid, M.G. Kanatzidis, Nat. Chem. 3, 160–166 (2011)

    CAS  Google Scholar 

  16. K. Biswas, J. He, I.D. Blum, C.I. Wu, T.P. Hogan, D.N. Seidman, V.P. Dravid, M.G. Kanatzidis, Nature 489, 414–418 (2012)

    CAS  Google Scholar 

  17. L.D. Zhao, S. Hao, S.H. Lo, C.I. Wu, X. Zhou, Y. Lee, H. Li, K. Biswas, T.P. Hogan, C. Uher, C. Wolverton, V.P. Dravid, M.G. Kanatzidis, J. Am. Chem. Soc. 135, 7364–7370 (2013)

    CAS  Google Scholar 

  18. R. Nunna, P. Qiu, M. Yin, H. Chen, R. Hanus, Q. Song, T. Zhang, M.-Y. Chou, M.T. Agne, J. He, G.J. Snyder, X. Shi, L. Chen, Energy Environ. Sci. 10, 1928–1935 (2017)

    CAS  Google Scholar 

  19. E.S. Toberer, C.A. Cox, S.R. Brown, T. Ikeda, A.F. May, S.M. Kauzlarich, G.J. Snyder, Adv. Funct. Mater. 18, 2795–2800 (2008)

    CAS  Google Scholar 

  20. Z.-Y. Li, J.-F. Li, Adv. Energy Mater. 4, 1300937 (2014)

    Google Scholar 

  21. C. Chang, M. Wu, D. He, Y. Pei, C.-F. Wu, X. Wu, H. Yu, F. Zhu, K. Wang, Y. Chen, L. Huang, J.-F. Li, J. He, L.-D. Zhao, Science 360, 778–783 (2018)

    CAS  Google Scholar 

  22. L.D. Zhao, S.H. Lo, Y. Zhang, H. Sun, G. Tan, C. Uher, C. Wolverton, V.P. Dravid, M.G. Kanatzidis, Nature 508, 373–377 (2014)

    CAS  Google Scholar 

  23. W.-J. Jung, I.-H. Kim, Met. Mater. Int. 24, 415–421 (2018)

    CAS  Google Scholar 

  24. P. Gao, X. Lu, I. Berkun, R.D. Schmidt, E.D. Case, T.P. Hogan, Appl. Phys. Lett. 105, 202104 (2014)

    Google Scholar 

  25. D. Kato, K. Iwasaki, M. Yoshino, T. Yamada, T. Nagasaki, J. Solid State Chem. 258, 93–98 (2018)

    CAS  Google Scholar 

  26. J. de Boor, T. Dasgupta, H. Kolb, C. Compere, K. Kelm, E. Mueller, Acta Mater. 77, 68–75 (2014)

    Google Scholar 

  27. G. Kim, H. Lee, J. Kim, J.W. Roh, I. Lyo, B.W. Kim, K.H. Lee, W. Lee, Ceram. Int. 43, 12979–12982 (2017)

    CAS  Google Scholar 

  28. A.L.S. Jeremy, M. Higgins, I.A. Guzei, S. Jin, J. Am. Chem. Soc. 130, 16086–16094 (2008)

    Google Scholar 

  29. W.-D. Liu, Z.-G. Chen, J. Zou, Adv. Energy Mater. 8, 1800056 (2018)

    Google Scholar 

  30. H.W. Knott, M.H. Mueller, L. Heaton, Acta Crystallogr. 23, 549–555 (1967)

    CAS  Google Scholar 

  31. Y. Miyazaki, D. Igarashi, K. Hayashi, T. Kajitani, K. Yubuta, Phys. Rev. B 78, 214104 (2008)

    Google Scholar 

  32. M.S.I. Kawasumi, I. Nishida, K. Masumoto, J. Mater. Sci. 16, 355–366 (1981)

    CAS  Google Scholar 

  33. G. Kim, H.J. Rim, K.H. Lee, J.W. Roh, W. Lee, Ceram. Int. 45, 19538–19541 (2019)

    CAS  Google Scholar 

  34. Z. Li, J.F. Dong, F.H. Sun, Asfandiyar, Y. Pan, S.F. Wang, Q. Wang, D. Zhang, L. Zhao, J.F. Li, Adv. Sci. 5, 1800626 (2018)

    Google Scholar 

  35. X. Chen, S.N. Girard, F. Meng, E. Lara-Curzio, S. Jin, J.B. Goodenough, J. Zhou, L. Shi, Adv. Energy Mater. 4, 1400452 (2014)

    Google Scholar 

  36. J.I. Tani, H. Kido, Phys. B 364, 218–224 (2005)

    CAS  Google Scholar 

  37. J.-I. Tani, H. Kido, Intermetallics 15, 1202–1207 (2007)

    CAS  Google Scholar 

  38. S.K. Bux, M.T. Yeung, E.S. Toberer, G.J. Snyder, R.B. Kaner, J.-P. Fleurial, J. Mater. Chem. 21, 12259–12266 (2011)

    CAS  Google Scholar 

  39. S. Battiston, S. Fiameni, M. Saleemi, S. Boldrini, A. Famengo, F. Agresti, M. Stingaciu, M.S. Toprak, M. Fabrizio, S. Barison, J. Electron. Mater. 42, 1956–1959 (2013)

    CAS  Google Scholar 

  40. J.E. Lee, S.H. Cho, M.W. Oh, B. Ryu, S.J. Joo, B.S. Kim, B.K. Min, H.W. Lee, S.D. Park, Electron. Mater. Lett. 10, 807–811 (2014)

    CAS  Google Scholar 

  41. S. Muthiah, B. Sivaiah, B. Gahtori, K. Tyagi, A.K. Srivastava, B.D. Pathak, A. Dhar, R.C. Budhani, J. Electron. Mater. 43, 2035–2039 (2014)

    CAS  Google Scholar 

  42. K. Mitra, G.K. Goyal, E. Rathore, K. Biswas, S. Vitta, S. Mahapatra, T. Dasgupta, Phys. Status Solidi A 215, 1700829 (2018)

    Google Scholar 

  43. S. Muthiah, J. Pulikkotil, A.K. Srivastava, A. Kumar, B.D. Pathak, A. Dhar, R.C. Budhani, Appl. Phys. Lett. 103, 053901 (2013)

    Google Scholar 

  44. Q.S. Meng, W.H. Fan, R.X. Chen, Z.A. Munir, J. Alloys Compd. 509, 7922–7926 (2011)

    CAS  Google Scholar 

  45. H. Kamila, P. Sahu, A. Sankhla, M. Yasseri, H.-N. Pham, T. Dasgupta, E. Mueller, J. de Boor, J. Mater. Chem. A 7, 1045–1054 (2019)

    CAS  Google Scholar 

  46. X. Tang, G. Wang, Y. Zheng, Y. Zhang, K. Peng, L. Guo, S. Wang, M. Zeng, J. Dai, G. Wang, X. Zhou, Scr. Mater. 115, 52–56 (2016)

    CAS  Google Scholar 

  47. J. de Boor, U. Saparamadu, J. Mao, K. Dahal, E. Müller, Z. Ren, Acta Mater. 120, 273–280 (2016)

    Google Scholar 

  48. U. Saparamadu, J. de Boor, J. Mao, S. Song, F. Tian, W. Liu, Q. Zhang, Z. Ren, Acta Mater. 141, 154–162 (2017)

    CAS  Google Scholar 

  49. G.N. Isachenko, A.Y. Samunin, E.A. Gurieva, M.I. Fedorov, D.A. Pshenay-Severin, P.P. Konstantinov, M.D. Kamolova, J. Electron. Mater. 45, 1982 (2016)

    CAS  Google Scholar 

  50. W. Liu, K. Yin, X. Su, H. Li, Y. Yan, X. Tang, C. Uher, Intermetallics 32, 352–361 (2013)

    Google Scholar 

  51. D. Berthebaud, F. Gascoin, J. Solid State Chem. 202, 61–64 (2013)

    CAS  Google Scholar 

  52. S.M. Choi, T.H. An, W.S. Seo, C. Park, I.H. Kim, S.U. Kim, J. Electron. Mater. 41, 1071–1076 (2012)

    CAS  Google Scholar 

  53. D.B. Migas, V.L. Shaposhnikov, A.B. Filonov, V.E. Borisenko, N.N. Dorozhkin, Phys. Rev. B 77, 075205 (2008)

    Google Scholar 

  54. D.K. Shin, S.W. You, I.H. Kim, J. Korean Phys. Soc. 64, 1412–1415 (2014)

    CAS  Google Scholar 

  55. G. Bernard-Granger, M. Soulier, H. Ihou-Mouko, C. Navone, M. Boidot, J. Leforestier, J. Simon, J. Alloys Compd. 618, 403–412 (2015)

    CAS  Google Scholar 

  56. S. Muthiah, R.C. Singh, B.D. Pathak, A. Dhar, Scr. Mater. 119, 60–64 (2016)

    CAS  Google Scholar 

  57. S. Muthiah, R.C. Singh, B.D. Pathak, P.K. Avasthi, R. Kumar, A. Kumar, A.K. Srivastava, A. Dhar, Nanoscale 10, 1970–1977 (2018)

    CAS  Google Scholar 

  58. X. Chen, A. Weathers, D. Salta, L. Zhang, J. Zhou, J.B. Goodenough, L. Shi, J. Appl. Phys. 114, 173705 (2013)

    Google Scholar 

  59. S.A. Barczak, R.A. Downie, S.R. Popuri, R. Decourt, M. Pollet, J.W.G. Bos, J. Solid State Chem. 227, 55–59 (2015)

    CAS  Google Scholar 

  60. Y. Miyazaki, H. Hamada, K. Hayashi, K. Yubuta, J. Electron. Mater. 46, 2705–2709 (2016)

    Google Scholar 

  61. G. Liu, Q. Lu, X. Zhang, J. Zhang, Y. Shi, J. Electron. Mater. 41, 1450–1455 (2011)

    Google Scholar 

  62. H. Nagai, H. Hamada, K. Hayashi, Y. Miyazaki, J. Electron. Mater. 48, 1902–1908 (2019)

    CAS  Google Scholar 

  63. H. Lee, G. Kim, B. Lee, J. Kim, S.-M. Choi, K.H. Lee, W. Lee, Scr. Mater. 135, 72–75 (2017)

    CAS  Google Scholar 

  64. X. She, X. Su, H. Du, T. Liang, G. Zheng, Y. Yan, R. Akram, C. Uher, X. Tang, J. Mater. Chem. C 3, 12116–12122 (2015)

    CAS  Google Scholar 

  65. S. Ghodke, N. Hiroishi, A. Yamamoto, H. Ikuta, M. Matsunami, T. Takeuchi, J. Electron. Mater. 45, 5279–5284 (2016)

    CAS  Google Scholar 

  66. T.K.T. Homma, N. Saito, S. Ghodke, T. Takeuchi, J. Alloys Compd. 776, 8–15 (2019)

    CAS  Google Scholar 

  67. Z. Gao, Z. Xiong, J. Li, C. Lu, G. Zhang, T. Zeng, Y. Ma, G. Ma, R. Zhang, K. Chen, T. Zhang, Y. Liu, J. Yang, L. Cao, K. Jin, J. Mater. Chem. A 7, 3384–3390 (2019)

    CAS  Google Scholar 

  68. G. Kim, S.W. Kim, H.J. Rim, H. Lee, J. Kim, J.W. Roh, B.-W. Kim, K.H. Lee, W. Lee, Scr. Mater. 162, 402–407 (2019)

    CAS  Google Scholar 

  69. N. Satyala, D. Vashaee, Appl. Phys. Lett. 100, 073107 (2012)

    Google Scholar 

  70. N. Satyala, D. Vashaee, J. Appl. Phys. 112, 093716 (2012)

    Google Scholar 

  71. P. Norouzzadeh, Z. Zamanipour, J.S. Krasinski, D. Vashaee, J. Appl. Phys. 112, 124308 (2012)

    Google Scholar 

  72. K. Yin, X. Su, Y. Yan, H. Tang, M.G. Kanatzidis, C. Uher, X. Tang, Scr. Mater. 126, 1–5 (2017)

    CAS  Google Scholar 

  73. T. Itoh, A. Tominaga, Mater. Trans. 57, 1088–1093 (2016)

    CAS  Google Scholar 

  74. M. Ishikawa, T. Nakamura, S. Hirata, T. Iida, K. Nishio, Y. Kogo, Jpn. J. Appl. Phys. 54, 07JC03 (2015)

    Google Scholar 

  75. N. Farahi, S. Prabhudev, M. Bugnet, G.A. Botton, J.R. Salvador, H. Kleinke, J. Electron. Mater. 45, 6052–6058 (2016)

    CAS  Google Scholar 

  76. N. Farahi, S. Prabhudev, M. Bugnet, G.A. Botton, J. Zhao, J.S. Tse, J.R. Salvador, H. Kleinke, RSC Adv. 5, 65328–65336 (2015)

    CAS  Google Scholar 

  77. G. Kim, H. Lee, H.J. Rim, J. Kim, K. Kim, J.W. Roh, S.-M. Choi, B.-W. Kim, K.H. Lee, W. Lee, J. Alloys Compd. 769, 53–58 (2018)

    CAS  Google Scholar 

  78. G. Kim, H.J. Rim, H. Lee, J. Kim, J.W. Roh, K.H. Lee, W. Lee, J. Alloys Compd. 801, 234–238 (2019)

    CAS  Google Scholar 

  79. T. Yi, S. Chen, S. Li, H. Yang, S. Bux, Z. Bian, N.A. Katcho, A. Shakouri, N. Mingo, J.P. Fleurial, N.D. Browning, S.M. Kauzlarich, J. Mater. Chem. 22, 24805–24813 (2012)

    CAS  Google Scholar 

  80. B. Zhang, T. Zheng, Q. Wang, Y. Zhu, H.N. Alshareef, M.J. Kim, B.E. Gnade, J. Alloys Compd. 699, 1134–1139 (2017)

    CAS  Google Scholar 

  81. D.Y.N. Truong, H. Kleinke, F. Gascoin, Dalton Trans. 43, 15092–15097 (2014)

    CAS  Google Scholar 

  82. W.-D. Liu, X.-L. Shi, R. Moshwan, Q. Sun, L. Yang, Z.-G. Chen, J. Zou, J. Mater. Chem. C 7, 7212–7218 (2019)

    CAS  Google Scholar 

  83. R. Zhao, F. Guo, Y. Shu, X. Zhang, Q. Lu, J. Zhang, JOM 66, 2298–2308 (2014)

    CAS  Google Scholar 

  84. X. Chen, J. Zhou, J.B. Goodenough, L. Shi, J. Mater. Chem. C 3, 10500–10508 (2015)

    CAS  Google Scholar 

  85. M. Saleemi, A. Famengo, S. Fiameni, S. Boldrini, S. Battiston, M. Johnsson, M. Muhammed, M.S. Toprak, J. Alloys Compd. 619, 31–37 (2015)

    CAS  Google Scholar 

  86. Y. Pei, H. Wang, G.J. Snyder, Adv. Mater. 24, 6125–6135 (2012)

    CAS  Google Scholar 

  87. G. Bernard-Granger, C. Navone, J. Leforestier, M. Boidot, K. Romanjek, J. Carrete, J. Simon, Acta Mater. 96, 437–451 (2015)

    CAS  Google Scholar 

  88. W. Liu, X. Tang, H. Li, J. Sharp, X. Zhou, C. Uher, Chem. Mater. 23, 5256–5263 (2011)

    CAS  Google Scholar 

  89. X. Liu, T. Zhu, H. Wang, L. Hu, H. Xie, G. Jiang, G.J. Snyder, X. Zhao, Adv. Energy Mater. 3, 1238–1244 (2013)

    CAS  Google Scholar 

  90. L. Zheng, X. Zhang, H. Liu, S. Li, Z. Zhou, Q. Lu, J. Zhang, F. Zhang, J. Alloys Compd. 671, 452–457 (2016)

    CAS  Google Scholar 

  91. W. Liu, X. Tang, H. Li, K. Yin, J. Sharp, X. Zhou, C. Uher, J. Mater. Chem. 22, 13653–13661 (2012)

    CAS  Google Scholar 

  92. N. Farahi, S. Prabhudev, G.A. Botton, J.R. Salvador, H. Kleinke, ACS Appl. Mater. Interfaces 8, 34431–34437 (2016)

    CAS  Google Scholar 

  93. W. Liu, H. Chi, H. Sun, Q. Zhang, K. Yin, X. Tang, Q. Zhang, C. Uher, Phys. Chem. Chem. Phys. 16, 6893–6897 (2014)

    CAS  Google Scholar 

  94. A.U. Khan, N. Vlachos, T. Kyratsi, Scr. Mater. 69, 606–609 (2013)

    CAS  Google Scholar 

  95. K. Yin, X. Su, Y. Yan, Y. You, Q. Zhang, C. Uher, M.G. Kanatzidis, X. Tang, Chem. Mater. 28, 5538–5548 (2016)

    CAS  Google Scholar 

  96. W. Liu, J. Zhou, Q. Jie, Y. Li, H.S. Kim, J. Bao, G. Chen, Z. Ren, Energy Environ. Sci. 9, 530–539 (2016)

    CAS  Google Scholar 

  97. W. Liu, H.S. Kim, S. Chen, Q. Jie, B. Lv, M. Yao, Z. Ren, C.P. Opeil, S. Wilson, C.W. Chu, Z. Ren, Proc. Natl. Acad. Sci. U. S. A. 112, 3269–3274 (2015)

    CAS  Google Scholar 

  98. U. Saparamadu, J. Mao, K. Dahal, H. Zhang, F. Tian, S. Song, W. Liu, Z. Ren, Acta Mater. 124, 528–535 (2017)

    CAS  Google Scholar 

  99. J. Mao, Y. Wang, B. Ge, Q. Jie, Z. Liu, U. Saparamadu, W. Liu, Z. Ren, Phys. Chem. Chem. Phys. 18, 20726–20737 (2016)

    CAS  Google Scholar 

  100. N. Farahi, S. Prabhudev, G.A. Botton, J. Zhao, J.S. Tse, Z. Liu, J.R. Salvador, H. Kleinke, J. Alloys Compd. 644, 249–255 (2015)

    CAS  Google Scholar 

  101. X. Zhou, G. Wang, H. Chi, X. Su, J.R. Salvador, W. Liu, X. Tang, C. Uher, J. Electron. Mater. 41, 1589–1594 (2012)

    Google Scholar 

  102. X. Hu, M.R. Barnett, A. Yamamoto, J. Alloys Compd. 649, 1060–1065 (2015)

    CAS  Google Scholar 

  103. Y. Pei, Z.M. Gibbs, A. Gloskovskii, B. Balke, W.G. Zeier, G.J. Snyder, Adv. Energy Mater. 4, 1400486 (2014)

    Google Scholar 

  104. X. Shi, X. Shi, Y. Li, Y. He, L. Chen, Q. Li, J. Appl. Phys. 116, 245104 (2014)

    Google Scholar 

  105. L.S. Walker, V.R. Marotto, M.A. Rafiee, N. Koratkar, E.L. Corral, ACS Nano 5, 3182–3190 (2011)

    CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Research Foundation of Korea (NRF) Grant (2017R1A2A1A17069528) and Basic Science Research Program funded by the Korea Government (MSIT) and the Ministry of Education (NRF-2019R1A6A1A11055660).

Author information

Authors and Affiliations

  1. Department of Materials Science and Engineering, Yonsei University, Seoul, 03722, Republic of Korea

    Gwansik Kim, Hyunjun Shin, Jihyun Lee & Wooyoung Lee

Authors
  1. Gwansik Kim
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Hyunjun Shin
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Jihyun Lee
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Wooyoung Lee
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Wooyoung Lee.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Kim, G., Shin, H., Lee, J. et al. A Review on Silicide-Based Materials: Thermoelectric and Mechanical Properties. Met. Mater. Int. 27, 2205–2219 (2021). https://doi.org/10.1007/s12540-020-00609-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12540-020-00609-9

Keywords

Search

Navigation