Abstract
In the present study, a unique method has been designed and developed by integrating Test Procedure 1 (TP-1) Alcan test equipment with electromagnetic stirring (EMS). The investigation is mainly focused on the design of equipment, manufacturing and controlling the experimental parameters to manipulate the structure of the Al castings. The design allows aluminium melt to be solidified in TP-1 mould under directional and a combination of directional with forced convection solidification mechanism. The effect of electromagnetic stirring current or induced voltage on macrostructural morphology of pure aluminium has been reported. It was observed that with the increase in current/voltage, the columnar grains were replaced by the fine and equiaxed grains due to the induced force convection created by EMS. Temperature gradients were measured for each solidifying melt in TP1 mould. The variation in temperature gradient with respect to time duration for different values of current (6A, 9A and 11A) was investigated and it was correlated to change in macrostructure of the casting.
Similar content being viewed by others
References
Guan ,T., 2018.The influence of inter-cooling and electromagnetic stirring above liquidus on the formation of primary Al 3 Zr and Grain Refinement in an Al-0.2%Zr Alloy. Materials (Basel). 12, 1–10. https://doi.org/10.3390/ma12010022.
Haghayeghi,R.,Kapranos, P.,2013.An investigation on physical and chemical refinement of aerospace aluminium alloys.Mater.Lett.95,121124.https://doi:https://doi.org/10.1016/j.matlet.2012.12.
Guan,R.G.,Tie D.A., 2017.Review on grain refinement of aluminum alloys progresses, challenges and prospects. Acta Metall. Sin. (English Lett.). 3, 409–432, .https://doi:https://doi.org/10.1007/s40195-017-0565-8.
Rao, A.A., Murty B.S., Chakraborty M., 1997.Role of zirconium and impurities in grain refinement aluminium with Al- Ti-B. Mater. Sci. Technol. 13,769–777.
Li Y., Liu Z., Xia Q., and Liu Y.,2007.Grain refinement of the Al-Cu-Mg-Ag alloy with Er and Sc additions. Metall. Mater. Trans. A Phys. Metall. Mater. Sci.. 38 A, 2853–2858. https://doi.org/10.1007/s11661-007-9269-4.
Tzeng Y.C.,Jian S.Y.,2018.Effects of the addition of trace amounts of Sc on the microstructure and mechanical properties of Al-11.6Si alloys. Mater. Sci. Eng. A.723, 22–28.https://doi.org/10.1016/j.msea.2018.03.016.
Li P., Kandalova E.G., Nikitin V.I.,2005.Grain refining performance of Al-Ti master alloys with different microstructures.Mater.Lett.59,723727.https://doi:https://doi.org/10.1016/j.matlet. 2004.06.073.
Greer A.L., 2003. Grain refinement of alloys by inoculation of melts. Philos. Trans. R. Soc. Lond. A. 361, 479–495. https://doi.org/10.1098/rsta.2002.1147
Qiu D., Taylor J.A., Zhang M.X., Kelly P.M., 2007. A mechanism for the poisoning effect of silicon on the grain refinement of Al–Si alloys. Acta Mater.55, 1447–1456.
Aquilano D.,Costa E.,Genovese A.,Massaro F.R.,Rubbo M., 2003. Heterogeneous nucleation and growth of crystalline micro-bubbles around gas cavities formed in solution. Prog. Cryst. Growth Charact. Mater. 46, 59–84. https://doi.org/10.1016/S0960-8974(03)90002-7.
Campanella T., Charbon C., Rappaz M.,2004.Grain refinement induced by electromagnetic stirring: A dendrite fragmentation criterion. Metall. Mater. Trans. A Phys. Metall. Mater. Sci. 35 A, 3201–3210. https://doi.org/10.1007/s11661-004-0064-1.
Ramirez A., Qian M., Davis B., Wilks T., StJohn D.H.,2008.Potency of high-intensity ultrasonic treatment for grain refinement of magnesium alloys. Scr. Mater.59,19–22. https://doi.org/10.1016/j.scriptamat.2008.02.017.
Hellawell A., Liu S., Lu S.Z.,1993.Dendrite fragmentation and the effects of fluid flow in castings. Jom. 49,18–20. https://doi.org/10.1007/BF02914650.
Guan T.Y.,Zhang Z.F.,Bai Y.L., Wang P.,2017.Effect of A-EMS above liquidus temperature on structure refinement of Al-11%Zn-3%Mg-1%Cu-0.13%Zr alloy. Mater. Sci. Forum. 898 ,24–28. https://doi.org/10.4028/www.scientific.net/MSF.898.24.
Zoqui E.J., Paes M., Sadiqi E.S., 2002. Macro- and microstructure analysis of SSM A356 produced by electromagnetic stirring. J Mater Process Technol .120,365–373.
Metan V., Eigenfeld K., Rabiger D., Leonhardt M.,Eckert S., 2009.Grain size control in Al-Si alloys by grain refinement and electromagnetic stirring.J.Alloys Compd..487,163–172.https://doi.org/10.1016/j.jallcom.2009.08.032.
Mao W., Lin H., Bai Y., Gao S., 2007. New method for the preparation of semi-solid AlSi7Mg alloy slurry. J Univ Sci Technol Beijing .14, 56–60.
Tzamtzis S, Solidification Behaviour and Mechanical Properties of Cast Mg-alloys and Al-based Particulate Metal Matrix Composites Under Intensive Shearing (2011) [dissertation]. BCAST(WL), Brunel Univ. at West London.
Lu D., Jiang Y., Guan G., Li Z., Zhou R., 2007.Refinement of primary Si in hypereutectic Al-Si alloy by electromagnetic stirring.J. Mater. Process. Technol..189,13–18. https://doi.org/10.1016/j.jmatprotec.2006.12.008.
Kumar D.S., 2001. A textbook of heat and mass transfer. S. K. Kataria & Sons., 30–101.
Acknowledgements
The authors are thankful to the technical assistant Mr. Santosh Nagwanshi of Department of Metallurgical and Materials Engineering, NIT Raipur, for helping us during casting processes.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
No potential conflict of interest was reported by the authors.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Kundu, A., Patel, D., Biswas, P. et al. Design of Electromagnetic TP-1 Test Equipment to Study the Change in Aluminium Macrostructure Under External Field. Trans Indian Inst Met 74, 1819–1826 (2021). https://doi.org/10.1007/s12666-021-02269-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-021-02269-8