Abstract
The influence of compaction degree of synthetic vaterite, the metastable polymorph of calcium carbonate, on determined mechanical properties was investigated using nanoindentation instrument. Specimens for measurements were prepared as pressed pellets with the application of three different forces—40, 60 and 80 kN. The highest values of reduced modulus and hardness were detected for vateritic pellet pressed at 60 kN. For this specimen, reduced modulus and hardness were found to be in ranges 74–10 and 5.2–0.3 GPa, respectively. Observation with scanning electron microscope showed increase compactness of pellet’s microstructure and an increase in density and length of microcracks within vateritic pellets when higher pressing force was applied.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Tegethoff, F.W.: Calcium carbonate—from the cretaceous period into the 21st century, 1st edn. Birkhauser Verlag, Basel (2001)
Sigel, A., Sigel, H., Sigel, R.K.O.: Biomineralization: from nature to application, 1st edn. Wiley, Chichester (2008)
Van Driessche, A.E.S., Kellermeier, M., Benning, L.G., Gebauer, D.: New perspectives on mineral nucleation and growth: from solution precursors to solid materials. Springer, Cham (2017)
Calvaresi, M., Falini, G., Pasquini, L., Reggi, M., Fermani, S., Gazzadi, G.C., Frabboni, S., Zerbetto, F.: Morphological and mechanical characterization of composite calcite/SWCNT–COOH single crystals. Nanoscale 5, 6944–6949 (2013)
Ševčík, R., Šašek, P., Viani, A.: Physical and nanomechanical properties of the synthetic anhydrous crystalline CaCO3 polymorphs: vaterite, aragonite and calcite. J. Mater. Sci. 53, 4022–4033 (2018)
Ševčík, R., Hrbek, V.: Influence of sample preparation on determined nanomechanical properties of metastable calcium carbonate polymorphs. In: Gdoutos, E.E. (ed.) ICTAEM 2018, pp. 3–7. Springer, Cham (2019)
Tai, C.Y., Chen, F.-B.: Polymorphism of CaCO3 precipitated in a constant-composition environment. AIChE J. 44, 1790–1798 (1998)
Ren, D., Meyers, M.A., Zhou, B., Feng, Q.: Comparative study of carp otolith hardness: lapillus and asteriscus. Mater. Sci. Eng. C 33, 1876–1881 (2013)
Portugal, S.J., Bowen, J., Riehl, C.: A rare mineral, vaterite, acts as a shock absorber in the eggshell of a communally nesting bird. Ibis 160, 173–178 (2018)
Xiao, C., Li, M., Wang, B., Liu, M-F., Shao, C., Pan, H., Lu, Y., Xu, B-B., Li, S., Zhan, D., Jiang, Y., Tang, R., Liu, X.Y., Cölfen, H.: Total morphosynthesis of biomimetic prismatic-type CaCO3 thin films. Nat. Commun. 8, 1398–1406 (2017)
Ševčík, R., Pérez-Estébanez, M., Viani, A., Šašek, P., Mácová, P.: Characterization of vaterite synthesized at various temperatures and stirring velocities without use of additives. Powder Technol. 284, 265–271 (2015)
Dhami, N.K., Mukherjee, A., Reddy, M.S.: Micrographical, minerological and nano-mechanical characterisation of microbial carbonates from urease and carbonic anhydrase producing bacteria. Ecol. Eng. 94, 443–454 (2016)
Acknowledgements
The authors gratefully acknowledge support from the Czech Science Foundation GA ČR grant 17-05030S. We thank Mgr. Petra Mácová for help with preparation of testing specimens.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2019 Springer Nature Switzerland AG
About this paper
Cite this paper
Ševčík, R., Hrbek, V. (2019). Role of Compactness on Hardness and Reduced Modulus of Vaterite Determined with Nanoindentation. In: Gdoutos, E. (eds) Proceedings of the Second International Conference on Theoretical, Applied and Experimental Mechanics. ICTAEM 2019. Structural Integrity, vol 8. Springer, Cham. https://doi.org/10.1007/978-3-030-21894-2_1
Download citation
DOI: https://doi.org/10.1007/978-3-030-21894-2_1
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-030-21893-5
Online ISBN: 978-3-030-21894-2
eBook Packages: EngineeringEngineering (R0)