Abstract
With crystalline silicon photovoltaic (PV) modules being in the market for over three decades, investigation into usual causes and extent of module degradation after prolonged exposure in field conditions is now possible. Degradation phenomena vary significantly between cells, modules and installations, giving rise to different power degradation rates reported. The main defects observed in the field-aged PV modules include EVA browning, degradation of the antireflective coating, delamination between the glass-encapsulant and the cell-encapsulant interfaces, humidity ingress, corrosion of busbars and contacts, shunt paths, cracks/micro-cracks in the cell, damage of the glass and the back sealing and bypass diode failure. This study presents severe degradation effects observed in PV modules operating outdoors for over 20 years. In many of the cases investigated, different defects were found to coexist within the same cell or module, leading to more severe effects of optical/physical, thermal and electrical degradation phenomena, significantly reducing the PV power output. Other modules that exhibited extensive optical/physical degradation showed milder degradation in performance. Detection of module degradation was carried out in this study first through visual inspection and I-V curve analysis. Further, nondestructive diagnostic techniques were used such as infrared thermography for the identification of hot spots and these were seen to be mainly linked to resistive busbars and contacts and electroluminescence imaging for the identification of shunts and other defects. The detection, diagnosis and monitoring of such defects is of great importance for a deeper understanding of the complex ageing mechanisms that take place after prolonged PV exposure in field conditions, and the identification of underlying causes, assisting the early identification of defects and the extension of the energy life of PV systems.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Wohlgemuth J (2012) IEC 61215: What it is and isn’t. 2012 PV Module Reliability Workshop. NREL/PR-5200-54714
Jordan DC, Kurtz SR (2012) Photovoltaic degradation rates—an analytical review. NREL/JA-5200-51664
Sharma V, Chandel SS (2013) Performance and degradation analysis for long term reliability of solar photovoltaic systems: a review. Renew Sustain Energy Rev 27:753–767
Meyer EL, van Dyk EE (2004) Assessing the reliability and degradation of photovoltaic module performance parameters. IEEE Transact Reliab 53(1):83–92
Kaplani E (2012) Detection of degradation effects in field-aged c-Si solar cells through IR thermography and digital image processing. Intl J Photoenergy 2012:1–11. doi:10.1155/2012/396792. (Art. no. 396792)
Sander M, Henke B, Schweizer S, Ebert M, Bagdahn J (2010) PV module defect detection by combination of mechanical and electrical analysis methods. Proceedings of theIEEE 35th Photovoltaic Specialists Conference, 20–25 June 2010, Honolulu
Yan F, Johnston S, Al-Jassim M, Zaunbrecher K, Sidelkheir O, Blosse A (2011) Defect-band emission photoluminescence imaging on multi-crystalline Si solar cells. Proceedings of the 37th IEEE Photovoltaic Specialists Conference, June 19–24 2011, Seattle, Washington. NREL/CP-5200-50725
Breitenstein O, Rakotoniaina JP, Al Rifai MH, Werner M (2004) Shunt types in crystalline silicon solar cells. Prog Photovolt: Res Appl 12:529–538
Kaplani E (2012) Degradation effects in sc-Si PV modules subjected to natural and induced ageing after several years of field operation. J Eng Sci Technol Rev 5(4):18–23
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2016 Springer International Publishing Switzerland
About this chapter
Cite this chapter
Kaplani, E. (2016). PV Cell and Module Degradation, Detection and Diagnostics. In: Sayigh, A. (eds) Renewable Energy in the Service of Mankind Vol II. Springer, Cham. https://doi.org/10.1007/978-3-319-18215-5_35
Download citation
DOI: https://doi.org/10.1007/978-3-319-18215-5_35
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-18214-8
Online ISBN: 978-3-319-18215-5
eBook Packages: EnergyEnergy (R0)