Enhanced photocatalytic properties of Bi2MoO6 nanoplates deposited with intermetallic AgPd nanoparticles by photoreduction method

  • Published:
Research on Chemical Intermediates Aims and scope Submit manuscript

Abstract

Bi2MoO6 nanoplates modified with intermetallic AgPd nanoparticles synthesized by photoreduction deposition method were used for visible-light-driven photodegradation of rhodamine B. The as-synthesized AgPd/Bi2MoO6 nanocomposites were identified by XRD. The 2θ diffraction angle of the (111) plane of pure metallic cubic Ag at 38.11° of heterostructure 10% Ag/Bi2MoO6 nanocomposites shifted to a higher diffraction angle at 38.17° of heterostructure 10% Ag0.7Pd0.3/Bi2MoO6 nanocomposites. TEM images of the as-synthesized nanocomposites showed good metallic Ag and intermetallic AgPd nanoparticles with particle size of 10–12 nm which were fully supported on top of Bi2MoO6 nanoplates. Bi2MoO6 nanoplates deposited with intermetallic AgPd nanoparticles show significant photocatalytic activity better than Ag/Bi2MoO6 and Bi2MoO6 due to the formation of AgPd/Bi2MoO6 Schottky barrier.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. S. Liu, J. Chen, D. Liu, L. Shan, X. Zhang, J. Nanopart. Res. 21(8), 191 (2019)

    Article  Google Scholar 

  2. M. Yaghoubi-berijani, B. Bahramian, S. Zargari, Res. Chem. Intermed. 46(1), 197 (2020)

    Article  CAS  Google Scholar 

  3. Z. Zhang, Y. Wang, X. Zhang, C. Zhang, Y. Wang, H. Zhang, C. Fan, Chem. Pap. 72(10), 2413 (2018)

    Article  CAS  Google Scholar 

  4. R. Zhang, Q. Han, Y. Li, T. Zhang, Y. Liu, K. Zeng, C. Zhao, J. Mater. Sci. 54(22), 14157 (2019)

    Article  CAS  Google Scholar 

  5. A. Phuruangrat, T. Klangnoi, P. Patiphatpanya, P. Dumrongrojthanath, S. Thongtem, T. Thongtem, Optik 212, 164674 (2020)

    Article  CAS  Google Scholar 

  6. K. Liu, Z.D. Chang, W.J. Li, P. Che, H.L. Zhou, Sci. China Chem. 55(9), 1770 (2012)

    Article  CAS  Google Scholar 

  7. Q.I. Zwane, S. Moeno, L.N. Dlamini, Appl. Nanosci. 9(4), 539 (2019)

    Article  CAS  Google Scholar 

  8. S.S. Lee, B.T. Huy, N.T.K. Phuong, D.K. Tung, Y.I. Lee, Korean J. Chem. Eng. 36(10), 1716 (2019)

    Article  CAS  Google Scholar 

  9. Z. Kása, K. Saszet, A. Dombi, K. Hernádi, L. Baia, K. Magyari, Z. Pap, Mater. Sci. Semicond. Process. 74, 21 (2018)

    Article  Google Scholar 

  10. Z. Dai, F. Qin, H. Zhao, J. Ding, Y. Liu, R. Chen, ACS Catal. 6(5), 3180 (2016)

    Article  CAS  Google Scholar 

  11. J. Ren, W. Wang, M. Shang, S. Sun, E. Gao, A.C.S. Appl, Mater. Interfaces 3(7), 2529 (2011)

    Article  CAS  Google Scholar 

  12. H. He, W. Wang, C. Xu, S. Yang, C. Sun, X. Wang, Y. Yao, N. Mi, W. Xiang, S. Li, G. Liu, Sci. Total Environ. 730, 139100 (2020)

    Article  CAS  PubMed  Google Scholar 

  13. X. Li, X. Mao, X. Zhang, Y. Wang, Y. Wang, H. Zhang, X. Hao, C. Fan, Sci. China Chem. 58(3), 457 (2015)

    Article  CAS  Google Scholar 

  14. H. Li, Z. Zheng, M. Liu, H. Jiang, D. Hu, X. Zhang, L. Xia, X. Geng, J. Lu, X. Cheng, Y. Wan, P. Yang, Appl. Surf. Sc. 510, 145468 (2020)

    Article  CAS  Google Scholar 

  15. B.E. Sanabria-Arenas, A. Mazare, J. Yoo, N.T. Nguyen, S. Hejazi, H. Bian, M.V. Diamanti, M.P. Pedeferri, P. Schmuki, Electrochim. Acta 292, 865 (2018)

    Article  CAS  Google Scholar 

  16. Y. Lu, J. Zhang, L. Ge, C. Han, P. Qiu, S. Fang, J. Colloid Interface Sci. 483, 146 (2016)

    Article  CAS  PubMed  Google Scholar 

  17. S.G. Khasevani, N. Faroughi, M.R. Gholami, Mater. Res. Bull. 126, 110838 (2020)

    Article  Google Scholar 

  18. M. Nischk, P. Mazierski, Z. Wei, K. Siuzdak, N.A. Kouame, E. Kowalska, H. Remita, A. Zaleska-Medynska, Appl. Surf. Sci. 387, 89 (2016)

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  19. Powder Diffract. File, JCPDS-ICDD, 12 Campus Boulevard, Newtown Square, PA 19073–3273, U.S.A., (2001)

  20. S. Sa-nguanprang, A. Phuruangrat, T. Thongtem, S. Thongtem, Russ. J. Inorg. Chem. 64(12), 1600 (2019)

    Article  CAS  Google Scholar 

  21. L. Arfaoui, F. Janene, S. Kouass, S. Mignard, F. Touati, H. Dhaouadi, Russ. J. Inorg. Chem. 64(13), 1687 (2019)

    Article  CAS  Google Scholar 

  22. A.B. Shishmakov, Y.V. Mikushina, O.V. Koryakova, L.A. Petrov, Russ. J. Inorg. Chem. 64(6), 864 (2019)

    Article  CAS  Google Scholar 

  23. A. Phuruangrat, P. Keereesaensuk, K. Karthik, P. Dumrongrojthanath, N. Ekthammathat, S. Thongtem, T. Thongtem, J. Inorg. Organomet. Polym. Mater. 30(2), 322 (2020)

    Article  CAS  Google Scholar 

  24. N.A. McDowell, K.S. Knight, P. Lightfoot, Chem. Eur. J. 129(5), 1493 (2006)

    Article  Google Scholar 

  25. L. Zhang, W. Wang, L. Zhou, H. Xu, Small 3(9), 1618 (2007)

    Article  CAS  PubMed  Google Scholar 

  26. E.C. Doluel, U. Kartal, T. Dikici, M. Yurddaskal, J. Electron. Mater. 49(6), 3849 (2020)

    Article  CAS  Google Scholar 

  27. J.J. Zhong, Y.H. Wang, J. Electron. Mater. 49(6), 3804 (2020)

    Article  CAS  Google Scholar 

  28. A. Phuruangrat, K. Rabiabdee, S. Thongtem, T. Thongtem, Dig. J. Nanomater. Bios. 14(2), 351 (2019)

    Google Scholar 

  29. X.Y. Zhu, Z.S. Lv, J.J. Feng, P.X. Yuan, L. Zhang, J.R. Chen, A.J. Wang, J. Colloid Interf. Sci. 516, 355 (2018)

    Article  CAS  Google Scholar 

  30. Y. Zhang, H. Fan, M. Li, H. Tian, Dalton Trans. 42(36), 13172 (2013)

    Article  CAS  PubMed  Google Scholar 

  31. A. Phuruangrat, S. Thongtem, T. Thongtem, Appl. Phys. A 126(3), 245 (2020)

    Article  CAS  Google Scholar 

  32. Y.G. Feng, H.J. Niu, L.P. Mei, J.J. Feng, K.M. Fang, A.J. Wang, J. Colloid Interface Sci. 575, 425 (2020)

    Article  CAS  PubMed  Google Scholar 

  33. H.Y. Chen, M.X. Jin, L. Zhang, A.J. Wang, J. Yuan, Q.L. Zhang, J.J. Feng, J. Colloid Interface Sci. 543, 1 (2019)

    Article  CAS  PubMed  Google Scholar 

  34. W. Jiang, X. Zhang, X. Gong, F. Yan, Z. Zhang, Int. J. Smart Nano Mater. 1(4), 278 (2010)

    Article  CAS  Google Scholar 

  35. H.M. Sung-Suh, J.R. Choi, H.J. Hah, S.M. Koo, Y.C. Bae, J. Photochem. Photobio. A 163(1–2), 37 (2004)

    Article  CAS  Google Scholar 

  36. N. Xiao, S. Li, S. Liu, B. Xu, Y. Li, Y. Gao, L. Ge, G. Lu, Chin. J. Catal. 40(4), 352 (2019)

    Article  CAS  Google Scholar 

  37. C. Wan, L. Zhou, L. Sun, L. Xu, D. Cheng, F. Chen, X. Zhan, Y. Yang, Chem. Eng. J. 396(14), 125229 (2020)

    Article  CAS  Google Scholar 

  38. L. Xiao, Y. Jun, B. Wu, D. Liu, T.T. Chuong, J. Fan, G.D. Stucky, J. Mater. Chem. A 5, 6382 (2017)

    Article  CAS  Google Scholar 

  39. X. Liu, D. Astruc, Adv. Mater. 29(16), 1605305 (2017)

    Article  Google Scholar 

  40. Y.J. Thong, J.H. Beh, J.C. Lai, T.H. Lim, ACS Omega 5(23), 13719 (2020)

    Article  Google Scholar 

  41. N. Waiskopf, Y. Ben-Shahar, M. Galchenko, I. Carmel, G. Moshitzky, H. Soreq, U. Banin, Nano Lett. 16(7), 4266 (2016)

    Article  CAS  PubMed  Google Scholar 

  42. H. Liang, Z. Jia, H. Zhang, X. Wang, J. Wang, Appl. Surf. Sci. 422, 1 (2017)

    Article  CAS  Google Scholar 

  43. H. Liang, S. Liu, H. Zhang, X. Wang, J. Wang, RSC Adv. 8(24), 13625 (2018)

    Article  CAS  Google Scholar 

  44. J. Wang, K. Chen, Y. Shen, X. Wang, Y. Guo, X. Zhou, R. Bai, Res. Chem. Intermed. 44(5), 3061 (2018)

    Article  CAS  Google Scholar 

  45. M. Tasviri, N. Miri, N. Mohaghegh, Res. Chem. Intermed. 45(3), 1039 (2019)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

The research was supported through the Faculty of Science Research Fund, Faulty of Science, Prince of Songkla University, Thailand, Contract no.1-2563-02-001.

Author information

Authors and Affiliations

  1. Department of Materials Science and Technology, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla, 90112, Thailand

    Piyada Suebsom & Anukorn Phuruangrat

  2. Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, 50200, Thailand

    Somchai Thongtem

  3. Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai, 50200, Thailand

    Somchai Thongtem & Titipun Thongtem

  4. Department of Chemistry, Faculty of Science, Chiang Mai University, Chiang Mai, 50200, Thailand

    Titipun Thongtem

Authors
  1. Piyada Suebsom
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Anukorn Phuruangrat
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Somchai Thongtem
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Titipun Thongtem
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Anukorn Phuruangrat or Titipun Thongtem.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Suebsom, P., Phuruangrat, A., Thongtem, S. et al. Enhanced photocatalytic properties of Bi2MoO6 nanoplates deposited with intermetallic AgPd nanoparticles by photoreduction method. Res Chem Intermed 47, 2357–2372 (2021). https://doi.org/10.1007/s11164-021-04417-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11164-021-04417-7

Keywords

Search

Navigation