Powders of YBa2Cu4O8 (“124”) were prepared via solid state reaction of Y2O3, BaCO3, and CuO. The mixed precursors were heated in flowing oxygen of reduced total pressure, followed by cooling and annealing at 750°C under ambient pressure oxygen. The procedure produced orthorhombic 124 as the main phase, with YBa2Cu3Ox (“123”) as a minor impurity phase. Phase purity improved, and nearly phase-pure 124 was obtained, upon annealing the as-calcined powder in flowing oxygen at 800°C.
Similar content being viewed by others
References
H. W. Zandbergen, R. Gronsky, K. Wang, and G. Thomas, Nature 331, 596 (1988).
T. Kogure et al., Physica C 156, 45 (1988).
A. F. Marshall et al., Phys. Rev. B37, 9353 (1988).
H. W. Zandbergen and G. Thomas, Phys. Stat. Sol. A105. 207 (1988).
P. Marsh, R. M. Fleming, M. L. Mandich, A. M. Desantalo, J. Kwo, M. Hong, and L. G. Martinez-Miranda, Nature 334, 141 (1988).
J. Karpinski, E. Kaldis, E. Jilek, S. Rusiecki, and B. Bucher, Nature 336. 660 (1988).
D. E. Morris, N. G. Asner, J. H. Nickel, R. L. Sid, J. Y. T. Wei, and J. E. Post, Physica C 152, 287 (1989).
U. Balachandran, M. E. Biznek, J. W. Tomlins, B. W. Veal, and R. B. Poeppel, submitted to Physica C (1989).
D. E. Morris et al., Phys. Rev. B39, 7347 (1989).
U. Balachandran et al., Mater. Lett. (December 1989).
R. J. Cava et al., Nature 332, 328 (1989).
P. K. Gallagher, Advan. Ceram. Mater. 2, 632 (1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Balachandran, U., Biznek, M.E., Goretta, K.C. et al. Processing and Fabrication of YBa2Cu4O8 and YBa2Cu4O8/YBa2Cu3Ox Composites. MRS Online Proceedings Library 169, 373–376 (1989). https://doi.org/10.1557/PROC-169-373
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-169-373