Results of an investigation aimed at developing a technique by which the fracture toughness of a thin film or small volume can be determined in nanoindentation experiments are reported. The method is based on the radial cracking which occurs when brittle materials are deformed by a sharp indenter such as a Vickers or Berkovich diamond. In microindentation experiments, the lengths of radial cracks have been found to correlate reasonably well with fracture toughness, and a simple semi-empirical method has been developed to compute the toughness from the crack lengths. However, a problem is encountered in extending this method into the nanoindentation regime with the standard Berkovich indenter in that there are well defined loads, called cracking thresholds, below which indentation cracking does not occur in most brittle materials. We have recently found that the problems imposed by the cracking threshold can be largely overcome by using an indenter with the geometry of the corner of a cube. For the cube-corner indenter, cracking thresholds in most brittle materials are as small as 1 mN (∼ 0.1 grams). In addition, the simple, well-developed relationship between toughness and crack length used for the Vickers indenter in the microindentation regime can be used for the cube-corner indenter in the nanoindentation regime provided a different empirical constant is used.
Similar content being viewed by others
References
G.M. Pharr and W.C. Oliver, MRS Bulletin 17, 28 (1992).
W.C. Oliver, MRS Bulletin 11, 15 (1986).
M.F. Doerner and W.D. Nix, J. Mater. Res. 1, 601 (1986).
W.C. Oliver and G.M. Pharr, J. Mater. Res. 7, 1564 (1992).
M.J. Mayo and W.D. Nix, Acta Metall. 36, 2183 (1988).
B.R. Lawn, A.G. Evans, and D.B. Marshall, J. Am. Ceram. Soc. 63, 574 (1980).
G.R. Anstis, P. Chantikul, B.R. Lawn, and D.B. Marshall, J. Am. Ceram Soc. 64, 533 (1981)
J. Lankford, and D.L. Davidson, J. Mater. Sci. 14, 1662 (1979).
K. Hirao and M. Tomozawa, J. Am. Ceram. Soc. 70, 497 (1987).
A. Arora, D.B. Marshall, B.R. Lawn, and M.V. Swain, J. Non-Cryst. Sol. 31, 415 (1979).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Harding, D.S., Oliver, W.C. & Pharr, G.M. Cracking During Nanoindentation and its Use in the Measurement of Fracture Toughness. MRS Online Proceedings Library 356, 663–668 (1994). https://doi.org/10.1557/PROC-356-663
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-356-663