Abstract
Room temperature visible and IR light electroluminescence (EL) has been obtained from Er-doped GaN Schottky barrier diodes. The GaN was grown by molecular beam epitaxy on Si substrates using solid sources (for Ga and Er) and a plasma source for N2. Transparent contacts utilizing indium tin oxide were employed. Strong green light emission was observed under reverse bias due to electron impact excitation of the Er atoms. Weaker emission was present under forward bias. The emission spectrum consists of two narrow green lines at 537 and 558 nm and minor peaks at 413, 461, 665, and 706 nm. There is also emission at 1000 nm and 1540 nm in the IR. The green emission lines have been identified as Er transitions from the 2H11/2 and 4S3/2 levels to the 4I15/2 ground state. The IR emission lines have been identified as transitions from the 4I13/2 and 4I13/2 levels to the 4I15/2 ground state. EL intensity for visible and IR light has a sub-unity power law dependence on bias current. An external quantum efficiency of 0.1% has also been demonstrated under a reverse bias current of 3.85 mA.
Similar content being viewed by others
References
S. Nakamura and G. Fasol, The Laser Diode, Springer Verlag, Berlin (1997), p. 215.
E. Downing, L. Hesselink, J. Ralston and R. Macfarlane, Science 273, 1185 (August 1996).
A.C. Tropper, J.N. Carter, R.D.T. Lauder, D.C. Hanna, S.T. Davey, and D. Szebesta, J. Opt. Soc. Am. B 11 (5), 886 (May 1994).
H. Ennen, G. Pomrenke, A. Axmann, K. Eisele, W. Haydl, and J. Schneider, Appl. Phys. Lett. 46 (4), 381 (February 1985).
G. Franzo and F. Priolo, Appl. Phys. Lett. 64, 2235 (April 1994).
B. Zheng, J. Michel, F. Y. G. Ren, L. C. Kimerling, D. C. Jacobson, and J. M. Poate, Appl. Phys. Lett. 64, 2842 (May 1994).
S. Lombardo, S. U. Campisano, G.N. van den Hoven, and A. Polman, J. Appl. Phys. 77, 6504 (June 1995)
C. X. Du, W. X. Ni, K. B. Joelsson, and G. V. Hansson, Appl. Phys. Lett. 71, 1023 (August 1997).
S. Coffa, G. Franzo, and F. Priolo, MRS Bulletin, 25 (April 1998).
R. G. Wilson and R. N. Schwartz, C. R. Abernathy and S. J. Pearton, N. Newman, M. Rubin, and T. Fu, J. M. Zavada, Appl. Phys. Lett. 65 (8), 992 (August 1994).
S. Kim, S. J. Rhee, D. A. Turnbull, E. E. Reuter, X. Li, J. J. Coleman, and S. G. Bishop, Appl. Phys. Lett. 71 (2), 231 (July 1997).
S. Kim, S. J. Rhee, D. A. Tumbull, X. Li, J. J. Coleman, and S. G. Bishop, Appl. Phys. Lett. 71 (18), 2662 (November 1997).
D. M. Hansen, R. Zhang, N. R. Perkins, S. Safvi, L. Zhang, K. L. Bray, and T. F. Kuech, Appl. Phys. Lett. 72 (10), 1244 (March 1998).
E. Silkowski, G. S. Pomrenke, Y. K. Yeo and R. L. Hengehold, Physica Scripta T69, 276 (1997).
J. T. Torvik, C. H. Qiu, R. J. Feuerstein and J. I. Pankove, F. Namavar, J. Appl. Phys. 81 (9), 6343 (May 1997).
C. H. Qiu, M. W. Leksono, and J. I. Pankove, J. T. Torvik and R. J. Feuerstein, F. Namavar, Appl. Phys. Lett. 66 (5), 562 (January 1995).
M. Zavada and D. Zhang, Solid-State Electron. 38, 1285 (1995).
T. Torvik, R. J. Feuerstein, J. I. Pankove, C. H. Qiu, and, F. Namavar, Appl. Phys. Lett. 69, 2098 (September 1996).
J. M. Zavada, M. Thaik, U. Hommerich, J.D. Mackenzie, C. R. Abernathy, Electrochem. Soc. 98-11, 193rd Meeting, Abstract no. 535, (Spring 1998).
A. J. Steckl and R. Birkhahn, Appl. Phys. Lett. 73 (12), 1700 (1998).
R. Birkhahn and A. J. Steckl, Appl. Phys. Lett. 73 (14), 2143 (1998).
A. J. Steckl, M. Garter, R. Birkhahn, J. Scofield, Appl. Phys. Lett. 73 (17), 2450 (1998).
M. Garter, J. Scofield, R. Birkhahn, A.J. Steckl, Appl. Phys. Lett. 74 (Jan. 11, 1998)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Garter, M., Birkhahn, R., Steckl, A.J. et al. Visible and Infrared Rare-Earth Activated Electroluminescence From Erbium Doped GaN. MRS Online Proceedings Library 537, 113 (1998). https://doi.org/10.1557/PROC-537-G11.3
Published:
DOI: https://doi.org/10.1557/PROC-537-G11.3