Abstract
ESCA examination of films formed on Cr-Co alloys after immersion in 0.1M NaCl for 24 h has shown that the thickness of passive films decreased with an increase in chromium content. Surface films consisted of chromium and cobalt oxides as Cr2O3 and CoO. The amount of CoO in the surface film of the alloy was decreased with an increase in chromium but Cr2O3 was found at a greater depth in the passive film at any composition. Cr2O3 was a major component of the surface film when the chromium content in the alloy was 10% or higher. Electrochemical techniques according to ASTM G59 and ASTM G5 were used for the determination of the relative corrosion rate. Both Co-10 wt.% Cr and Co-30 wt.% Cr alloys investigated showed a lower corrosion rate than the Co-5 wt.% Cr alloy. Corrosion rate measured could be correlated to the surface film composition and structure as determined by ESCA.
Similar content being viewed by others
References
A.S. Lim, A. Atrens: Appl. Phys. A 53, 273–281 (1991)
S. Jin, A. Atrens: Appl. Phys. A 42, 149–165 (1987)
C.D. Wagner, W.M. Riggs, L.E. Davis, J.F. Meulder: Handbook of X-ray Photoelectron Spectroscopy, ed. by G.E. Muilenberg (Perkin-Elmer, Eden Prairie 1978)
N.S. McIntyre: In Practical Surface Analysis, ed. by D. Briggs, N.P. Seah (Wiley, Chichester 1983) p. 397
K. Asami, K. Hashimoto: Corros. Sci. 17, 559–570 (1977)
I. Ikemoto, K. Ishii, S. Kinoshita, H. Kuroda, M.A. Alario Franco, J.M. Thomas: J. Solid State Chem. 17, 425–430 (1976)
E. Desimoni, C. Malitesta, P.G. Zambonin, J.C. Riviere: Surf. Int. Anal. 13, 173–179 (1988)
N.S. McIntyre, D.D. Johnston, L.L. Coatsworth, R.D. Davidson: Surf. Int. Anal. 15, 265–272 (1990)
K. Asami, K. Hashimoto, S. Shimodaira: Corros. Sci. 17, 713–723 (1977)
J.C. Langevoort, I. Sutherland, L.J. Hanekamp, P.J. Gellings: Appl. Surf. Sci. 28, 167–179 (1987)
H.J. Mathieu, D. Landolt: Corros. Sci. 26, 547–559 (1986)
S. Mischler, H.J. Mathieu, D. Landolt: Surf. Int. Anal. 11, 182–188 (1988)
C.D. Wagner: J. Electron Spectrosc. Relat. Phenom. 32, 99 (1983)
P. Bruesch, K. Müller, A. Atrens, H. Neff: Appl. Phys. A 38, 1–18 (1985)
ASTM G59: Standard Practice for Conducting Potentiodynamic Polarisation Resistance Measurements
ASTM G5: Standard Practice for Standard Reference. Method for Making Potentiostatic and Potentiodynamic Anodic Polarisation Measurements
L. Bjornkvist, I. Olefjord: Eurocorr 87, European Corros. Meeting, Karlsruhe, Germany (April 1987)
R. Holm, S. Storp: Appl. Phys. 9, 217 (1976)
H.H. Uhlig, R.B. Mears: In Corrosion Handbook, ed. by H.H. Uhlig (Wiley, New York 1948) p. 20