Abstract
Relative motion between mating surfaces at elevated temperatures often causes substantial material degradation due to friction and wear. Conventionally, solid lubricants have been used to reduce wear damage and friction drag under extreme conditions where liquid lubricants do not function properly. The recent trend towards higher operating temperatures in advanced power generating systems, i.e. turbomachinery, gas turbines, and hot adiabatic diesel engines, has imposed severe limitations on the currently available solid lubricants. The unusually aggressive conditions in these systems phased out most conventional solid lubricants and gave impetus to the search for more efficient materials. This paper discusses the lubricating characteristics of four different groups of materials known to provide lubricity under elevated temperature conditions. These groups are polymers, laminar solids, metal fluorides and metal oxides. Polymer lubricants are efficient lubricants within the range from room temperature to about 300 °C. Laminar solids extend that range to about 450 °C. Graphite, also a laminar solid, is an exception since it can offer excellent lubricity beyond 450 °C in the form of gaseous oxidation products. Stable fluorides and metal oxides are useful lubricants between 500 and 1000 °C, though their performance is rather poor at lower temperatures.
Similar content being viewed by others
References
R. L. Fusaro, “Effect of Thermal Aging on the Tribological Properties of Polyimide Film and Polyimide Bonded Graphite Films”, NASA, TM-79045 (1979).
M. N. Garods andB. D. Mcconnell, “Development of High-Load, High Temperature, Self Lubricating Composites. Part IV: Formation and Performance of Best Compositions”, ASLE Reprint No. 81-LC-3A-6, ASLE Special Publication SP-9 (1982).
H. E. Sliney andR. L. Johnson, Graphite Fibre-Polyimide Composites for Spherical Bearings to 340 °C, NASA TN-D-7078 (1972).
R. L. Fusaro andH. E. Sliney, Friction and Wear Behavior of Graphite Fiber Reinforced Polyimide Composites,ASLE Trans. 21(4) (1978) 337–43.
H. E. Sliney andT. P. Jacobson, Performance of Graphite Fiber Reinforced Polyimide Composites in Self-Aligning Plain Bearings to 315°C,Lubr. Eng. 31(12) (1975) 609–13.
K. Friedrich, Sliding wear performance of different polyimide formulations,Tribology International 22, 1 (1989) 25.
M. Gardos andB. McConnell, Development of High Load, High Temperature, Self Lubricating Composite-Part II: Reinforcement Selection, ASLE Reprint No. 81-LC-3A-4, ASLE Special Publication SP-9 (1982).
R. L. Fusaro, Polyimides. Tribological Properties and Their Use as Lubricants, NASA TM-82959 (1982).
R. Fusaro, Evoluation of several polymer materials for use as solid lubricants in space,Tribology Transactions 31, 2 (1988) 174–81.
H. E. Sliney, Solid Lubricant Materials for High Temperatures, A Review,Tribology International 15 (5) (1982) 303–15.
R. M. Gresham, Solid lubricants: unique products for unique lubrication,Lubrication Engineering 44, 2 (1988) 143–45.
H. E. Sliney, High Temperature Solid Lubricants, Part 2: Polymers and Fluoride Coatings and Composites,Mech. Eng. March (1974) 34–9.
L. B. Sargent, ‘Lubricants’ in “Tribology; Friction, Lubrication, and Wear”, edited by A. Z. Szeri (Hemisphere Publishing Corpn, Washington D.C., 1980) Ch. 9, pp. 427–76.
J. B. Thompson, G. C. Turrel, andB. W. Sandt,J. Appl. Phys. 26 (1955) 1088–92.
F. Clauss, “Solid lubricants and self-lubricating solids”, (Academic Press, New York, 1972).
B. Bhushan andD. Wilcock, ‘Frictional behavior of polymeric compositions in dry sliding’ in “Friction and Traction”, Proceedings of the 7th Leeds-Lyon Symposium on Tribology, Institute of Tribology, University of Leeds, UK, 9–12 September, 1980, (Westbury House, IPC Science and Technology Press. Guildford, 1980).
R. H. Savage,J. Appl. Phys. 19 (1948) 1–10.
H. E. Sliney,Mech. Eng. 2 (1974) 18–22.
A. R. Lansdown, “Lubrication, A practical guide to lubricant selection” (Pergamon, Oxford, 1982).
J. B. Peace, ‘Solid Lubricants’ in “Lubrication and Lubricants”, edited by E. R. Braithwait (Elsevier, Amsterdam, 1967).
M. B. Peterson andR. L. Johnson, Friction Studies of Graphite and Mixtures of Graphite with Several Metallic Oxides and Salts at Temperatures to 1000 °F, NASA TN-3657 (1957).
D. Klamann, “Lubricants and related products”, (Verlag Chemi GMbH, Weinheim, 1984).
M. N. Gardos andB. D. Mcconnell, “Development of High Load, High Temperature, Self Lubricating Composite. Part III: Additives Selections”, ASLE Reprint No. 81-LC-3A-5, ASLE Special Publications SP-9 (1982).
K. A. Kuriakose andJ. I. Margrave,Inorganic Chemistry 4 (1965) 1639–41.
R. L. Fusaro andH. E. Sliney, Graphite Fluoride (CF x ) n -A New Solid Lubricant,ASLE Trans. 13 (1) (1970) 56–65.
W. O. Winer,Wear 10 (1967) 422–52.
S. Ross andA. Sussman,J. Phys. Chem. 59 (1955) 889–92.
M. Gardos,Tribology Transactions 31, 2 (1988) 214–27.
P. W. Centers,Wear 122, 1 (1988) 7–102.
M. Gardos,Tribology Transactions 31, 2 (1988) 214.
M. T. Lavik, T. M. Medev, andG. D. Moore,ASLE Trans. 11 (1968) 44–55.
H. E. Sliney, in “Proceedings of the U.S.A.F. Aerospace Fluids and Lubricants Conference edited by P. M. Ku, (16–19 April 1963, South West Research Institute, 1963) 350–67.
H. F. Barry, andJ. P. Binkelman,Lubrication Engng 22 (1966) 139–45.
A. W. J. DeGee, G. Solomon, andJ. H. Zatt,ASLE Trans. 8 (1965), 156–63.
G. Solomon, A. W. J. DeGee, andJ. H. Zatt,Wear 7 (1964), 87–101.
J. K. Lancaster,Wear 9 (1966) 169–88.
R. Kremith, J. Rosenbery, andV. Hopkins,Amer. Ceram. Soc. Bull. 47 (1968) 813–18.
S. Ramalingam, W. O. Winer, andS. Bair,Thin Solid Films 84 (1981) 273–79.
R. I. Christy,ibid. 73 (1980) 299–307.
H. A. Sundquist,ibid. 73 (1980) 309–14.
B. Stupp,ibid. 84 (1981) 257.
M. N. Gardos, in “Semi-annual Status Report No. 7. Executive Summary” (Hughes Aircraft Company, Culver City, CA 90230, Reporting Period 1 February 1982 to 30 September 1982).
E. Bergmann, G. Melet, C. Muller, andA. Simonvermont,Tribology International 14 (1981) 329–32.
F. Bowden andD. Tabor, “The friction and lubrication of solids”, Part II (Oxford University Press, London, 1964).
K. E. Demorest andA. F. Whitaker, Investigation of the Coefficient of Friction of Various Greases and Dry Film Lubricants at Ultra High Loads for the Saturn Hold-Down Arms, NASA TM-X-53331 (1965).
H. E. Sliney, T. M. Strom, andG. P. Allen, Fused Fluoride Coatings as Solid Lubricants in Liquid Sodium, Hydrogen, Vacuum, and Air, NASA TN-D-2348 (1964).
H. E. Sliney, T. N. Strom, andG. P. Allen,ASLE Trans. 8 (1965) 307–23.
H. E. Sliney, Rare Earth Fluorides and Oxides. An Exploratory Study of Their Use as Solid Lubricants at Temperatures to 1800 °F (1000 °C), NASA TM-D-5301 (1969).
H. E. Sliney, A Commentary on Solid Lubricants and Wear-Resistant Solids for Use in Extreme Environments, NASA TM-83042 (1982).
H. E. Sliney,ASLE Trans 9 (1966) 336–47.
H. E. Sliney, Solid Lubricants for Extreme Environment, NASA TM-X52214 (1966).
H. E. Sliney andR. L. Fusaro, Friction and Wear of Sintered Tungsten, Molybdenum, and Cobalt-Molybdenum Impregnated with a Fluoride Eutectic, NASA TN-6363 (1971).
H. E. Sliney andJ. W. Graham,J. Lubr. Techn. July (1975) 506–11.
H. Sliney,ASLE Trans. 9 (1966), 336–47.
I. Amato andP. C. Martinengo,ASLE Trans 16 (1973) 42–9.
R. L. Johnson andH. E. Sliney,Am. Ceram. Soc. Bull. 41 (1962) 504–08.
H. E. Sliney,ASLE Trans. 15 (1972) 177–83.
M. T. Lavik, B. D. McConnel, andG. D. Moore,J. Lubr. Tech. Jan. (1972) 12–18.
F. H. Stott andG. C. Wood, ‘The influence of oxidates in high-temperature wear’ in “High Temperature Corrosion” edited by R. Rapp (NACE, 1983) p. 406.
R. B. Waterhouse,Wear 100 (1984) 107.
F. H. Stott andG. C. Wood,Tribology International 11, 4 (1978) 211–18.
M. B. Peterson andR. L. Johnson,Lubrication Engng 13 (1957) 203–07.
H. E. Sliney, Lubricating Properties of Lead-Monoxide-Base Coatings of Various Compositions at Temperatures to 1250 °F, NASA Memo 3-2-59E (1959).
I. Amato andP. Martinengo,ASLE Trans. 17 (1974) 201–05.
H. E. Sliney andR. L. Johnson, Bonded Lead Monoxide Films as Solid Lubricants for Temperatures up to 1250 °F, NACA RM-E57B15 (1957).
H. E. Sliney, Effect of Sliding Velocity of Friction Properties and Endurance Life of Bonded Lead Monoxide Coatings at Temperatures Up to 1250 °F, NASA RM-E58B11 (1958).
M. B. Peterson, S. F. Murray, andJ. J. Florek,ASLE Trans. 2 (1969) 225–34.
M. B. Peterson, S. B. Calabrese, andB. Stupp, “Lubrication with Naturally Occurring Double Oxide Films”, Wear Science Corporation Final Report WSC-CR-82-10 (Prepared for Defense Advanced Research Projects Agency (DARPA), Arlington, VA 22209, 1982).
E. Rabinowicz andM. Imai, Basic Oxide as a High Temperature Lubricant, ASME Paper 61-11-17 (1961).
B. Bunshan,J. Lubr. Engng. 103 (1981) 218–27.
I. Amato, P. G. Gappelli andP. C. Martinengo,Wear 34 (1975) 65–75.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Allam, I.M. Solid lubricants for applications at elevated temperatures. J Mater Sci 26, 3977–3984 (1991). https://doi.org/10.1007/BF02402936
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02402936