Abstract
Photoelectrical properties of single ZnO nanowires have been investigated using photocurrent–voltage characteristics measurements varying with excitation photon energy and temperature. It is found that persistent photoconductivity (PPC) exists, and the PPC decreases with decreasing temperature. The temperature dependence of the PPC effect indicates that thermally activated return of electrons from shallow traps is responsible for the PPC phenomenon. The photosensitivity is found to be linear with the applied voltage, and it increases with decreasing temperature. A temperature dependence of photoconductivity gain was introduced to explain the experimental results.
Similar content being viewed by others
References
J.B.K. Law, J.T.L. Thong, Nanotechnology 19, 205502 (2008)
S.J. Chang, T.J. Hsueh, C.L. Hsu, Y.R. Lin, I.C. Chen, B.R. Huang, Nanotechnology 19, 095505 (2008)
Z.Y. Fan, J.G. Lu, Appl. Phys. Lett. 86, 123510 (2005)
J.M. Bao, M.A. Zimmler, F. Capasso, X.W. Wang, Z.F. Ren, Nano Lett. 6, 1719 (2006)
M.C. Jeong, B.Y. Oh, M.H. Ham, J.M. Myoung, Appl. Phys. Lett. 88, 202105 (2006)
Z.M. Liao, J. Xu, J.M. Zhang, D.P. Yu, Appl. Phys. Lett. 93, 023111 (2008)
Q.D. Zhao, T.F. Xie, L.L. Peng, Y.H. Lin, P. Wang, L. Peng, D.J. Wang, J. Phys. Chem. C 111, 17136 (2007)
M.H. Huang, S. Mao, H. Feick, H.Q. Yan, Y.Y. Wu, H. Kind, E. Weber, R. Russo, P.D. Yang, Science 292, 1897 (2001)
K. Keem, H. Kim, G.T. Kim, J.S. Lee, B. Min, K. Cho, M.Y. Sung, S. Kim, Appl. Phys. Lett. 84, 4376 (2004)
J. Suehiro, N. Nakagawa, S. Hidaka, M. Ueda, K. Imasaka, M. Higashihata, T. Okada, M. Hara, Nanotechnology 17, 2567 (2006)
C. Soci, A. Zhang, B. Xiang, S.A. Dayeh, D.P.R. Aplin, J. Park, X.Y. Bao, Y.H. Lo, D. Wang, Nano Lett. 7, 1003 (2007)
H. Kind, H.Q. Yan, B. Messer, M. Law, P.D. Yang, Adv. Mater. 14, 158 (2002)
J. Nayak, J. Kasuya, A. Watanabe, S. Nozaki, J. Phys.: Condens. Matter 20, 195222 (2008)
S.E. Ahn, H.J. Ji, K. Kim, G.T. Kim, C.H. Bae, S.M. Park, Y.K. Kim, J.S. Ha, Appl. Phys. Lett. 90, 153106 (2007)
Z.M. Liao, K.J. Liu, J.M. Zhang, J. Xu, D.P. Yu, Phys. Lett. A 367, 207 (2007)
Z.M. Liao, Z.K. Lv, Y.B. Zhou, J. Xu, J.M. Zhang, D.P. Yu, Nanotechnology 19, 335204 (2008)
H. Meier, Organic Semiconductors: Dark- and Photoconductivity of Organic Solids (Verlag Chemie GmbH, Weinheim, 1974)
A. Rose, Concepts in Photoconductivity and Allied Problems (Interscience, New York, 1963)
Z.M. Liao, H.Z. Zhang, Y.B. Zhou, J. Xu, J.M. Zhang, D.P. Yu, Phys. Lett. A 372, 4505 (2008)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Liao, ZM., Lu, Y., Xu, J. et al. Temperature dependence of photoconductivity and persistent photoconductivity of single ZnO nanowires. Appl. Phys. A 95, 363–366 (2009). https://doi.org/10.1007/s00339-008-5058-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-008-5058-1