Abstract
This work examines the possibility that the previously observed elastic yielding, i.e., nonquiescent relaxation after a large step shear (Ravindranath and Wang, Macromolecules 40:8031–8039, 2007) is due to an intrinsic experimental difficulty technically known as edge fracture. By redesigning the rheometric apparatus to eliminate edge failure, we show by an example of a well-entangled polymer solution that elastic yielding still occurs in the absence of any edge failure. We are also able to confirm that shear banding during large amplitude oscillatory shear (Ravindranath and Wang, J Rheol 52:341–358, 2008a) is an inherent rheological characteristic related to internal yielding of the entanglement network.
Similar content being viewed by others
References
Adams JM, Olmsted PD (2009a) Nonmonotonic models are not necessary to obtain shear banding phenomena in entangled polymer solutions. Phys Rev Lett 102:067801
Adams JM, Olmsted PD (2009b) Comment on “nonmonotonic models are not necessary to obtain shear banding phenomena in entangled polymer solutions”. Phys Rev Lett 103:219801 (author reply)
Boukany PE, Wang SQ (2009a) Shear banding or not in entangled DNA solutions depending on the level of entanglement. J Rheol 53:73–83
Boukany PE, Wang SQ (2009b) Exploring the transition from wall slip to bulk shearing banding in well-entangled DNA solutions. Soft Matter 5:780–789
Boukany PE, Hu YT, Wang SQ (2008) Observations of wall slip and shear banding in an entangled DNA solution. Macromolecules 41:2644–2650
De Gennes PG (2007) Melt fracture of entangled polymers. Eur Phys J E 23:3–5
Doi M, Edwards SF (1988) The theory of polymer dynamics, 2nd edn. Oxford University Press, New York
Ferry JD (1980) Viscoelastic properties of polymers. Wiley, New York
Galvin PT, Whorlow RW (1975) Studies of time effects in the flow of polymer melts using a biconical viscometer. J Appl Polym Sci 19:567–583
Graham RS, Likhtman AE, McLeish TCB (2003) Microscopic theory of linear, entangled polymer chains under rapid deformation including chain stretch and convective constraint release. J Rheol 47:1171–1200
Inn YW, Wissbrun KF, Denn MM (2005) Effect of edge fracture on constant torque rheometry of entangled polymer solutions. Macromolecules 38:9385–9388
Lodge AS (1964) Elastic liquids. An introductory vector treatment of finite-strain polymer rheology. Academic, London
Marrucci G (1996) Dynamics of entanglements: a nonlinear model consistent with the Cox–Merz rule. J Non-Newton Fluid Mech 62:279–289
Mead DW, Larson RG, Doi M (1998) A molecular theory for fast flows of entangled polymers. Macromolecules 31:7895–7914
Meissner J, Garbella RW, Hostettler J (1989) Measuring normal stress differences in polymer melt shear flow. J Rheol 33:843–864
Ravindranath S, Wang SQ (2007) What are the origins of stress relaxation behaviors in step shear entangled polymer solutions. Macromolecules 40:8031–8039
Ravindranath S, Wang SQ (2008a) Particle-tracking velocimetric investigation of large amplitude oscillatory shear behavior of entangled polymer solutions. J Rheol 52:341–358
Ravindranath S, Wang SQ (2008b) Banding in simple steady shear of entangled polymer solutions. Macromolecules 41:2663–2670
Ravindranath S, Wang SQ (2008c) Steady state measurements in stress plateau region of entangled polymer solutions: controlled-rate and controlled-stress modes. J Rheol 52:957–980
Schweizer T (2002) Measurement of the first and second normal stress differences in a polystyrene melt with a cone and partitioned plate tool. Rheol Acta 41:337–344
Schweizer T (2007) Shear banding during nonlinear creep with a solution of monodisperse polystyrene. Rheol Acta 46:629–637
Sui C, McKenna GB (2007) Instability of entangled polymers in cone and plate rheometry. Rheol Acta 46:877–888
Tapadia P, Wang SQ (2006) Direct visualization of continuous simple shear in non-Newtonian polymeric fluids. Phys Rev Lett 96:016001–004
Wang SQ (2009) Comment on “nonmonotonic models are not necessary to obtain shear banding phenomena in entangled polymer solutions”. Phys Rev Lett 103:219801–1 (Adams and Olmsted replied to our comment by carrying out a simulation with a “homogeneous” step strain of 3.0 that produces sinusoidal wave-like macroscopic motion after shear cessation in Fig. 2 (Adams and Olmsted 2009b). However, this starting condition is anything but homogeneous shear. Velocity field and therefore the deformation field were not completely a linear function of the gap distance in their Fig. 2)
Wang SQ, Ravindranath S, Boukany PE, Olechnowicz M, Quirk RP, Halasa A, Mays J (2006) Nonquiescent relaxation in entangled polymer liquids after step shear. Phys Rev Lett 97:187801–804
Wang YY, Wang SQ (2009) Yielding during startup deformation of entangled linear polymeric liquids. J Rheol 53:1389
Wang YY, Boukany PE, Wang SQ, Wang XR (2007) Elastic breakup in uniaxial extension of entangled polymer melts. Phys Rev Lett 99:237801–804
Acknowledgement
This work is supported, in part, by a grant (DMR-0821697) from the National Science Foundation.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, X., Wang, SQ. Elastic yielding after step shear and during LAOS in the absence of meniscus failure. Rheol Acta 49, 985–991 (2010). https://doi.org/10.1007/s00397-010-0465-6
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00397-010-0465-6