The Running-in Tribological Behavior of Pb-Free Brass and Its Effect on Microstructural Evolution

  • Original Paper
  • Published:
Tribology Letters Aims and scope Submit manuscript

Abstract

In this paper, the running-in tribological behavior of Pb-free brass (i.e., 64% copper and 36% Zinc) sliding against 100Cr6 under lubricated condition and its effect on grain refinement are investigated systematically. The sliding experiment is preformed using a tribometer based on in situ holography microscopy and radionuclide technique. After the tribological test, the friction pair is characterized using scanning electron microscopy and transmission electron microscopy in order to quantify the micrography, chemistry and microstructure. It is found that the curve of the friction coefficient exhibits two steep falls during the initial stage, while the real-time wear rates at these moments are relatively high. Then the test enters the dynamic stability stage due to equilibrium between the processes of strain hardening and recovery. The brass sliding experiment is carried out in the boundary lubrication region leading to dislocation movement and void formation due to plastic deformation. Moreover, an exceptional increase in two directional stacking faults is observed that extend and interdiffuse into each other. More importantly, as has been observed before, the coarse grains are considerably refined into nano-grains due to the accumulation of dislocation movement induced by repeated sliding test.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Nobel, C., Hofmann, U., Klocke, F., Veselovac, D., Puls, H.: Application of a new, severe-condition friction test method to understand the machining characteristics of Cu–Zn alloys using coated cutting tools. Wear 344–345, 58–68 (2015). https://doi.org/10.1016/j.wear.2015.10.016

    Article  Google Scholar 

  2. Liu, J., Wang, X.H., Ran, Q.N., Zhao, G., Zhu, X.X.: Microstructure and properties of Cu–3Ti–1Ni alloy with aging process. Trans. Nonferrous Metals Soc. China 26(12), 3183–3188 (2016). https://doi.org/10.1016/S1003-6326(16)64450-3

    Article  Google Scholar 

  3. Bagheri, G.A.: The effect of reinforcement percentages on properties of copper matrix composites reinforced with TiC particles. J. Alloys Compd. 676, 120–126 (2016). https://doi.org/10.1016/j.jallcom.2016.03.085

    Article  Google Scholar 

  4. Lu, Z.C., Zeng, M.Q., Xing, J.Q., Zhu, M.: Improving wear performance of CuSn5Bi5 alloys through forming self-organized graphene/Bi nanocomposite tribolayer. Wear 364–365, 122–129 (2016). https://doi.org/10.1016/j.wear.2016.07.014

    Article  Google Scholar 

  5. Feser, T., Stoyanov, P., Mohr, F., Dienwiebel, M.: The running-in mechanisms of binary brass studied by in situ topography measurements. Wear 303(1–2), 465–472 (2013). https://doi.org/10.1016/j.wear.2013.03.047

    Article  Google Scholar 

  6. Gane, N.: The effect of lead on the friction and machining of brass. Philos. Mag. A 43(3), 545–566 (2006). https://doi.org/10.1080/01418618108240394

    Article  Google Scholar 

  7. Environmental Protection Agency: Safety of Public Water Systems—The Safe Drinking Water Act (SDWA), came into effect on 31.12.2002. Public Health Service Act

  8. European Parliament and Council: Directive 2000/53/EC on End of Life Vehicles (ELV), came into effect on 18.09.2000. Gazette of the European Community, 269, 2000, pp. 34–42

  9. European Parliament and Council: Directive 2011/65/EU on Restriction of Hazardous Substances (RoHS2), revised form came into effect on 08.06.2011

  10. Bundesministerium für Gesundheit, Verbraucherschutz, Ernährung und Landwirtschaft: Verordnung zur Novellierung der Trinkwasserverordnung (TrinkwV2001), came into effect on 21. 05. 2001. Bundesgesetzblatt 24, 2001, pp. 959–980

  11. Zambrano, O.A., Aguilar, Y., Valdés, J., Rodríguez, S.A., Coronado, J.J.: Effect of normal load on abrasive wear resistance and wear micromechanisms in FeMnAlC alloy and other austenitic steels. Wear 348–349, 61–68 (2016). https://doi.org/10.1016/j.wear.2015.11.019

    Article  Google Scholar 

  12. Hernández Battez, A., González, R., Viesca, J.L., Fernández, J.E., Díaz Fernández, J.M., Machado, A., Chou, R., Riba, J.: CuO, ZrO2 and ZnO nanoparticles as antiwear additive in oil lubricants. Wear 265(3–4), 422–428 (2008). https://doi.org/10.1016/j.wear.2007.11.013

    Article  Google Scholar 

  13. AsadiKouhanjani, S., ZareBidaki, A., Akbari, A.: The effect of sliding speed and amount of loading on friction and wear behavior of Cu–0.65 wt%Cr alloy. J. Alloys Compd. 486(1–2), 319–324 (2009). https://doi.org/10.1016/j.jallcom.2009.06.129

    Article  Google Scholar 

  14. Dienwiebel, M., Pöhlmann, K.: Nanoscale evolution of sliding metal surfaces during running-in. Tribol. Lett. 27(3), 255–260 (2007). https://doi.org/10.1007/s11249-007-9216-y

    Article  Google Scholar 

  15. Nehl, E.: Wear test for bulk metal forming using a radionuclide technique. Wear 107(4), 329–341 (1986). https://doi.org/10.1016/0043-1648(86)90163-8

    Article  Google Scholar 

  16. Trdan, U., Skarba, M., Grum, J.: Laser shock peening effect on the dislocation transitions and grain refinement of Al–Mg–Si alloy. Mater. Charact. 97, 57–68 (2014). https://doi.org/10.1016/j.matchar.2014.08.020

    Article  Google Scholar 

  17. Korres, S., Dienwiebel, M.: Design and construction of a novel tribometer with online topography and wear measurement. Rev. Sci. Instrum. 81(6), 063904 (2010). https://doi.org/10.1063/1.3449334

    Article  Google Scholar 

  18. Scherge, M., Pöhlmann, K., Gervé, A.: Wear measurement using radionuclide-technique (RNT). Wear 254(9), 801–817 (2003). https://doi.org/10.1016/S0043-1648(03)00230-8

    Article  Google Scholar 

  19. Cao, H.M., Zhou, X., Li, X.Y., Lu, K.: Friction mechanism in the running-in stage of copper: from plastic deformation to delamination and oxidation. Tribol. Int. 115, 3–7 (2017). https://doi.org/10.1016/j.triboint.2017.05.027

    Article  Google Scholar 

  20. Jahanmir, S., Suh, N.P., Abrahamson, E.P.: The delamination theory of wear and the wear of a composite surface. Wear 32(1), 33–49 (1975). https://doi.org/10.1016/0043-1648(75)90203-3

    Article  Google Scholar 

  21. Suh, N.P.: The delamination theory of wear. Wear 25(1), 111–124 (1973). https://doi.org/10.1016/0043-1648(73)90125-7

    Article  Google Scholar 

  22. Moshkovich, A., Perfilyev, V., Bendikov, T., Lapsker, I., Cohen, H., Rapoport, L.: Structural evolution in copper layers during sliding under different lubricant conditions. Acta Mater. 58(14), 4685–4692 (2010). https://doi.org/10.1016/j.actamat.2010.05.001

    Article  Google Scholar 

  23. Moshkovich, A., Perfilyev, V., Meshi, L., Samuha, S., Cohen, S., Cohen, H., Laikhtman, A., Rapoport, L.: Friction, wear and structure of Cu samples in the lubricated steady friction state. Tribol. Int. 46(1), 154–160 (2012). https://doi.org/10.1016/j.triboint.2011.03.013

    Article  Google Scholar 

  24. Moshkovich, A., Perfilyev, V., Gorni, D., Lapsker, I., Rapoport, L.: The effect of Cu grain size on transition from EHL to BL regime (Stribeck curve). Wear 271(9), 1726–1732 (2011). https://doi.org/10.1016/j.wear.2010.12.052

    Article  Google Scholar 

  25. Lu, J.Z., Luo, K.Y., Zhang, Y.K., Sun, G.F., Gu, Y.Y., Zhou, J.Z., Ren, X.D., Zhang, X.C., Zhang, L.F., Chen, K.M., Cui, C.Y., Jiang, Y.F., Feng, A.X., Zhang, L.: Grain refinement mechanism of multiple laser shock processing impacts on ANSI 304 stainless steel. Acta Mater. 58(16), 5354–5362 (2010). https://doi.org/10.1016/j.actamat.2010.06.010

    Article  Google Scholar 

  26. Lychagin, D.V., Filippov, A.V., Novitskaia, O.S., Chumlyakov, Y.I., Kolubaev, E.A., Sizova, O.V.: Friction-induced slip band relief of Hadfield steel single crystal oriented for multiple slip deformation. Wear 374–375, 5–14 (2017). https://doi.org/10.1016/j.wear.2016.12.028

    Article  Google Scholar 

  27. Zhang, P., Qu, S., Yang, M.X., Yang, G., Wu, S.D., Li, S.X., Zhang, Z.F.: Varying tensile fracture mechanisms of Cu and Cu–Zn alloys with reduced grain size: from necking to shearing instability. Mater. Sci. Eng., A 594(Supplement C), 309–320 (2014). https://doi.org/10.1016/j.msea.2013.11.079

    Google Scholar 

  28. Fischer, A.: Subsurface microstructural alterations during sliding wear of biomedical metals. Modelling and experimental results. Comput. Mater. Sci. 46(3), 586–590 (2009). https://doi.org/10.1016/j.commatsci.2009.01.016

    Article  Google Scholar 

  29. Christian Greiner, Z.L.: Luis Strassberger, Peter Gumbsch: sequence of stages in the microstructure evolution in copper under mild reciprocating tribological loading. ACS Appl. Mater. Interfaces. 8, 15809–15819 (2016)

    Article  Google Scholar 

  30. Lu, J.Z., Luo, K.Y., Zhang, Y.K., Cui, C.Y., Sun, G.F., Zhou, J.Z., Zhang, L., You, J., Chen, K.M., Zhong, J.W.: Grain refinement of LY2 aluminum alloy induced by ultra-high plastic strain during multiple laser shock processing impacts. Acta Mater. 58(11), 3984–3994 (2010). https://doi.org/10.1016/j.actamat.2010.03.026

    Article  Google Scholar 

  31. Karthikeyan, S., Agrawal, A., Rigney, D.A.: Molecular dynamics simulations of sliding in an Fe–Cu tribopair system. Wear 267(5), 1166–1176 (2009). https://doi.org/10.1016/j.wear.2009.01.032

    Article  Google Scholar 

  32. Zhai, W.Z., Shi, X.L., Wang, M., Xu, Z.S., Yao, J., Song, S.Y., Wang, Y.F.: Grain refinement: a mechanism for graphene nanoplatelets to reduce friction and wear of Ni3Al matrix self-lubricating composites. Wear 310(1–2), 33–40 (2014). https://doi.org/10.1016/j.wear.2013.12.014

    Article  Google Scholar 

Download references

Acknowledgements

This work is funded by the National Natural Science Foundation of China (Project Nos. 51601021, 51441001) and the German Science Foundation DFG (Project No. DI 1494/4-1) and Natural Science Foundation of Jiangsu Province (Project No. BK20140262) and the Natural Science Foundation of Jiangsu Higher Education Institutions (17KJA460002) and China Postdoctoral Science Foundation (Project No. 2017M611718). The authors also wish to thank André Blockhaus for assistance with the in situ tribological experiments.

Author information

Authors and Affiliations

  1. School of Mechanical Engineering, Changzhou University, Gehu Road 1, Changzhou, 213164, Jiangsu, China

    Lin Liu & Zhichen Zhang

  2. Institute for Applied Materials, Karlsruhe Institute for Technology, Kaiserstraße 12, 76128, Karlsruhe, Germany

    Martin Dienwiebel

  3. Fraunhofer Institute for Mechanics of Materials IWM, Wöhlerstraße 11, 79108, Freiburg, Germany

    Martin Dienwiebel

  4. Jiangsu Key Laboratory of Green Process Equipment, Changzhou University, Gehu Road 1, Changzhou, 213164, Jiangsu, China

    Lin Liu & Zhichen Zhang

Authors
  1. Lin Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Zhichen Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Martin Dienwiebel
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Lin Liu or Martin Dienwiebel.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Liu, L., Zhang, Z. & Dienwiebel, M. The Running-in Tribological Behavior of Pb-Free Brass and Its Effect on Microstructural Evolution. Tribol Lett 65, 160 (2017). https://doi.org/10.1007/s11249-017-0943-4

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s11249-017-0943-4

Keywords

Search

Navigation