ZnO nanorods were prepared through a sol-gel process by adding various amounts of water at low temperature and atmospheric pressure conditions for application as a photocatalyst. The 1-D ZnO nanostructures can overcome fast recombination of photogenerated electrons and holes that inhibits photocatalytic efficiency. X-ray diffractometer and transmission electron microscopy measurements confirmed that the (002)/(100) intensity ratio increased from 0.83 to 1.34 and the morphology of the ZnO nanoparticles was changed from a spherical shape to nanorods with the addition of water. UV-vis spectroscopy showed a red shift from 360 nm to 371 nm, which indicates a decrease of the band gap energy. PL measurements of the ZnO nanorods showed a 103 times improvement of the NBE/DLE intensity ratio compared to the ZnO nanospheres. When the photocatalytic efficiency of the ZnO nanoparticles was estimated for the degradation of methylene blue dye under irradiation of UV light, the photocatalytic kinetic constant increased from 0.067 min−1 to 0.481 min−1. As a result, longer ZnO nanorods showed better photocatalytic performance.
Similar content being viewed by others
References
J. Wang, R. Chen, Y. Xia, G. Wang, H. Zhao, L. Xiang and S. Komarneni, Ceram. Int., 43, 1870 (2017).
J. Mishra, M. Jha, N. Kaur and A. K. Ganguli, Mater. Res. Bull., 102, 311 (2018).
S. G. Kumar and L. G. Devi, J. Phys. Chem. A, 115, 13211 (2011).
C. J. Chang, M. H. Hsu, Y. C. Weng, C. Y. Tsay and C. K. Lin, Thin Solid Films, 528, 167 (2013).
T. Di, B. Zhu, J. Zhang, B. Cheng and J. Yu, Appl. Surf. Sci., 389, 775 (2016).
L. Mao, H. Liu, S. Liu, Q. Ba, H. Wang, L. Gao, X. Li, C. Huang and W. Chen, Mater. Res. Bull., 93, 9 (2017).
M. R. D. Khaki, M. S. Shafeeyan, A. A. A. Raman and W. M. A. W. Daud, J. Environ. Manage., 198, 78 (2017).
R. Singh, K. Verma, A. Patyal, I. Sharma, P. B. Barman and D. Sharma, Solid State Sci., 89, 1 (2019).
E. Hong, T. Choi and J. H. Kim, Korean J. Chem. Eng., 32, 424 (2015).
B. Weng, M. Q. Yang, N. Zhang and Y. J. Xu, J. Mater. Chem. A, 2, 9380 (2014).
R. Raji and K. G. Gopchandran, J. Phys. Chem. Solids, 113, 39 (2018).
N. Huang, J. Shu, Z. Wang, M. Chen, C. Ren and W. Zhang, J. Alloys. Compd., 648, 919 (2015).
X. Zhang, J. Qin, Y. Xue, P. Yu, B. Zhang, L. Wang and R. Liu, Sci. Rep., 4, 4596 (2014).
Z. Liu, Z. G. Zhao and M. Miyauchi, J. Phys. Chem. C, 113, 17132 (2009).
S. Kato, Y. Hirano, M. Iwata, T. Sano, K. Takeuchi and S. Matsuzawa, Appl. Catal. B-Environ., 57, 109 (2005).
J. Zhang, L. Sun, H. Pan, C. Liao and C. Yan, New J. Chem., 26, 33 (2002).
P. X. Gao and Z. L. Wang J. Phys. Chem. B, 108, 7534 (2004).
J. J. Wu and S. C. Liu, Adv. Mater., 14, 215 (2002).
R. Liu, A. A. Vertegel, E. W. Bohannan, T. A. Sorenson and J. A. Switzer, Chem. Mater., 13, 508 (2001).
Y. W. Heo, V. Varadarajan, M. Kaufman, K. Kim, D. P. Norton, F. Ren and P. H. Fleming, Appl. Phys. Lett., 81, 3046 (2002).
H. Cheng-Liang, C. Shoou-Jinn, H. Hui-Chuan, L. Yan-Ru, H. Chorng-Jye, T. Yung-Kuan and I. Chen, IEEE T. Nanotechnology, 4, 649 (2005).
S. Yan, L. Wan, Z. Li and Z. Zou, Chem. Commun., 47, 5632 (2011).
Q. Jijun, L. Xiaomin, H. Weizhen, S. J. Park, H. K. Kim, Y. H. Han, J. H. Lee and Y. D. Kim, Nanotechnology, 20, 155603 (2009).
P. Banerjee, S. Chakrabarti, S. Maitra and B. K. Dutta, Ultrason. Sonochem., 19, 85 (2012).
Y. Jeong, J. Y. Kang, I. Kim, H. Jeong, J. K. Park, J. H. Park and J. C. Jung, Korean J. Chem. Eng., 33, 114 (2016).
B. Cheng, W. Shi, J. M. Russell-Tanner, L. Zhang and E. T. Samulski, Inorg. Chem., 45, 1208 (2006).
H. J. Jung, S. Lee, H. C. Choi and M. Y. Choi, Solid State Sci., 21, 26 (2013).
H. Wang, C. Xie and D. Zeng, J. Cryst. Growth, 277, 372 (2005).
Y. Chen, H. Zhao, B. Liu and H. Yang, Appl. Catal. B-Environ., 163, 189 (2015).
C. K. Frederik, T. Yi, T. Ralf and W. A. Jens, Nanotechnology, 19, 424013 (2008).
J. Bouclé, H. J. Snaith and N. C. Greenham, J. Phys. Chem. C, 114, 3664 (2010).
J. Q. Hu, Q. Li, N. B. Wong, C. S. Lee and S. T. Lee, Chem. Mater., 14, 1216 (2002).
S. Kundu, S. Sain, B. Satpati, S. R. Bhattacharyya and S. K. Pradhan, RSC Adv., 5, 23101 (2015).
A. McLaren, T. Valdes-Solis, G. Li and S. C. Tsang, J. Am. Chem. Soc., 131, 12540 (2009).
H. Çolak, E. Karaköse and G. Kartopu, J. Mater. Sci-Mater. El., 29, 11964 (2018).
L. Yanhong, W. Dejun, Z. Qidong, Y. Min and Z. Qinglin, J. Phys. Chem. B, 108, 3202 (2004).
Z. L. S. Seow, A. S. W. Wong, V. Thavasi, R. Jose, S. Ramakrishna and G. W. Ho, Nanotechnology, 20, 045604 (2008).
M. S. Mohajerani, A. Lak and A. Simchi, J. Alloys. Compd., 485, 616 (2009).
T. M. Shang, J. H. Sun, Q. F. Zhou and M. Y. Guan, Cryst. Res. Technol., 42, 1002 (2007).
L. Yang, P. W. May, L. Yin and T. B. Scott, Nanotechnology, 18, 215602 (2007).
J. Sun, J. Bian, H. Liang, J. Zhao, L. Hu, Z. Zhao, W. Liu and G. Du, Appl. Surf. Sci., 253, 5161 (2007).
Y. Liu, X. Yan, Z. Kang, Y. Li, Y. Shen, Y. Sun, L. Wang and Y. Zhang, Sci. Rep., 6, 29907 (2016).
K. Choi, T. Kang and S. G. Oh, Mater. Lett., 75, 240 (2012).
Q. Li, J. Bian, J. Sun, J. Wang, Y. Luo, K. Sun and D. Yu, Appl. Surf. Sci., 256, 1698 (2010).
J. Gupta, K. C. Barick and D. Bahadur, J. Alloys. Compd., 509, 6725 (2011).
J. Rouhi, M. Alimanesh, R. Dalvand, C. H. R. Ooi, S. Mahmud and M. R. Mahmood, Ceram. Int., 40, 11193 (2014).
S. A. Vanalakar, S. S. Mali, M. P. Suryawanshi, N. L. Tarwal, P. R. Jadhav, G. L. Agawane, K. V. Gurav, A. S. Kamble, S. W. Shin, A. V. Moholkar, J. Y. Kim, J. H. Kim and P. S. Patil, Opt. Mater., 37, 766 (2014).
C. B. Ong, L. Y. Ng and A. W. Mohammad, Renew. Sustain. Energy Rev., 81, 536 (2018).
G. He, B. Huang, Z. Lin, W. Yang, Q. He and L. Li, Crystals, 8, 152 (2018).
X. Chen, Z. Wu, D. Liu and Z. Gao, Nanoscale Res. Lett., 12, 143 (2017).
L. Y. Yang, S. Y. Dong, J. H. Sun, J. L. Feng, Q. H. Wu and S. P. Sun, J. Hazard. Mater., 179, 438 (2010).
Y. Zheng, L. Zheng, Y. Zhan, X. Lin, Q. Zheng and K. Wei, Inorg. Chem., 46, 6980 (2007).
A. Leelavathi, G. Madras and N. Ravishankar, Phys. Chem. Chem. Phys., 15, 10795 (2013).
Acknowledgements
This research was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education (2016R1A6A1A 03013422).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Seo, Y.S., Oh, SG. Controlling the recombination of electron-hole pairs by changing the shape of ZnO nanorods via sol-gel method using water and their enhanced photocatalytic properties. Korean J. Chem. Eng. 36, 2118–2124 (2019). https://doi.org/10.1007/s11814-019-0401-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11814-019-0401-0