Comparing the weldability of AA6013-T4 aluminium alloy on DP600 dual-phase steel with laser welding and resistance spot welding

  • Technical Paper
  • Published:
Journal of the Brazilian Society of Mechanical Sciences and Engineering Aims and scope Submit manuscript

Abstract

The welding of high-strength aluminium alloys on AHSS with laser beam welding (LBW) and resistance spot welding (ERW) is challenging due to the formation of brittle intermetallic phases. The weldability of a lap dissimilar joint between an AA6013-T4 aluminium alloy and a DP600 dual-phase steel with respect to microstructure and mechanical behaviour was investigated in this study. Microstructural analysis with optical microscopy shows that the ERW process did not show any significant dilution among the base materials. However, dilution and crack formation occurred in the fusion zone (FZ) during LBW. Martensite formed in the DP 600 dual-phase steel and liquation formed in the AA6013-T4 aluminium alloy within the heat-affected zone (HAZ) with both processes. X-ray diffraction and energy-dispersive X-ray spectroscopy analyses showed the formation of Fe3Al intermetallic phases at the interface between the FZ and HAZ with both welding processes. Tensile test results showed no differences between the strength limits for both processes with an average value of 68 MPa. However, the shear deformation was 62% higher in samples welded using ERW. This study shows that dissimilar joint welding of AA6013-T4 aluminium alloy to DP600 dual-phase steel is possible, despite the formation of the Fe3Al intermetallic phase, and that the ERW process is the most appropriate.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

Similar content being viewed by others

References

  1. American Welding Society, AWS D8.1M:2013 (2013) Specification for automotive weld quality—resistance spot welding of steel, Danvers. ISBN: 978-0-87171-910-2

  2. Atabaki MM, Nikodinovski M, Chenier P et al (2014) Welding of aluminum alloys to steels: an overview. J Manuf Sci Prod 14(2):59–78

    Google Scholar 

  3. Bakavos D, Chen Y, Babout L et al (2011) Material interactions in a novel pinless tool approach to friction stir spot welding thin aluminum sheet. Metall Mater Trans A 42:1266–1282

    Article  Google Scholar 

  4. Born P, Mayer B (2004) Structural bonding in automotive applications. Auto Technol 4:44–45

    Google Scholar 

  5. Bozzi S, Helbert-Etter AL, Baudin T, Criqui B et al (2010) Intermetallic compounds in Al 6016/IF-steel friction stir spot welds. Mater Sci Eng A 527(16–17):4505–4509

    Article  Google Scholar 

  6. Carvalho SM, Lima MSF (2012) Laser beam welding tempered 300M ultrahigh mechanical strength steel. J Braz Soc Mech Sci Eng 34(1):18–23

    Google Scholar 

  7. Ciupack Y, Pasternak H, Mette C (2017) Adhesive bonding in steel construction—challenge and innovation. Procedia Eng 172:186–193

    Article  Google Scholar 

  8. Correard GCC, Miranda GP, Lima MSF (2015) Development of laser beam welding of advanced high-strength steels. Int Adv Manuf Technol 83:1967–1977

    Article  Google Scholar 

  9. De Cooman BC, Chin K-G, Kim J (2011) High Mn TWIP steels for automotive applications. In: Chiaberge M (ed) New trends and developments in automotive system engineering. ISBN: 978-953-307-517-4. InTech. https://www.intechopen.com/books/new-trends-and-developments-in-automotive-system-engineering/high-mn-twip-steels-for-automotive-applications

  10. Dong D, Liu Y, Yang Y et al (2014) Microstructure and dynamic tensile behavior of DP600 dual phase steel joint by laser welding. Mater Sci Eng A 594:17–25

    Article  Google Scholar 

  11. Dursun T, Soutis C (2014) Recent developments in advanced aircraft aluminium alloys. Mater Des 56:862–871

    Article  Google Scholar 

  12. European Aluminum Association (2015) The aluminium automotive manual. https://www.european-aluminium.eu/media/1514/1-introduction_2015.pdf

  13. European Aluminum Association (2018) Aluminium in cars: unlocking the light-weighting potential. https://www.european-aluminium.eu/media/1326/aluminium-in-cars-unlocking-the-lightweighting-potential.pdf

  14. Harnando I, Arrizubieta JI, Lamikiz A et al (2018) Numerical model for predicting bead geometry and microstructure in laser beam welding of inconel 718 sheets. Metals 8(7):1–17

    Google Scholar 

  15. He X, Pearson I, Young K (2008) Self-pierce riveting for sheet materials: state of the art. J Mater Process Technol 199:27–36

    Article  Google Scholar 

  16. Hirsch J (2001) Aluminium in Innovative light-weight car design. Mater Trans 52(5):818–824

    Article  Google Scholar 

  17. Hutchinson A, Winfield PH, Morrey D (2013) Automotive structures: design for disassembly and the role of adhesive bonding. Mater Sci Forum 765:721–725

    Article  Google Scholar 

  18. Indhu R, Divya S, Tak M et al (2018) Microstructure development in pulsed laser welding of dual phase steel to aluminium alloy. Procedia Manuf 26:495–502

    Article  Google Scholar 

  19. Jia L, Schichun J, Yan S et al (2015) Effects of zinc on the laser welding of an aluminum alloy and galvanized steel. J Mater Process Technol 224:49–59

    Article  Google Scholar 

  20. Kim Y-G, Jo B-J, Kim J-S et al (2017) A study on dissimilar welding of aluminum alloy and advanced high strength steel by spot welding process. Int J Precis Eng Manuf 18(1):121–126

    Article  Google Scholar 

  21. Kou S (2002) Welding metallurgy, 2nd edn. Wiley, Hoboken

    Book  Google Scholar 

  22. Lan S, Liu X, Ni J (2016) Microstructural evolution during friction stir welding of dissimilar aluminum alloy to advanced high-strength steel. Int J Adv Manuf Technol 82:2183–2193

    Article  Google Scholar 

  23. Li X, Scherf A, Heilmaier M et al (2016) The Al-rich part of the Fe–Al phase diagram. J Phase Equilib Diff 37(2):162–173

    Article  Google Scholar 

  24. Loverborn D, Larsson JK, Persson K-A (2017) Weldability of aluminium alloys for automotive applications. Phys Procedia 89:89–99

    Article  Google Scholar 

  25. Lutz A (2015) Structural bonding of lightweight cars crash durable, safe and economical. Dow Automotive Systems, Horgen, pp 1–12

    Google Scholar 

  26. Ma J, Kong F, Carlson B, Kavokevic R (2013) Two-pass laser welding of galvanized high strength dual-phase steel for a zero-gap lap joint configuration. J Mater Process Technol 312:495–507

    Article  Google Scholar 

  27. Ma J, Harooni M, Carson B et al (2014) Dissimilar joining of galvanized high-strength steel to aluminum alloy in a zero-gap lap joint configuration by two-pass laser welding. Mater Des 58:390–401

    Article  Google Scholar 

  28. Miller WS, Zhuang L, Bottema J et al (2000) Recent development in aluminium alloys for the automotive industry. Mater Sci Eng A 280:37–49

    Article  Google Scholar 

  29. Meco S, Pardal G, Ganguly S, Williams S et al (2015) Application of laser in seam welding of dissimilar steel to aluminium joints for thick structural components. Opt Lasers Eng 2015:22–30

    Article  Google Scholar 

  30. Qui R, Satnonaka S, Iwamoto C (2009) Effect of interfacial reaction layer continuity on the tensile strength of resistance spot welded joints between aluminum alloy and steels. Mater Des 30(9):3686–3689

    Article  Google Scholar 

  31. Reil M, Morin D, Langseth M et al (2018) Connections between steel and aluminium using adhesive bonding combined with self-piercing riveting. In: 12th international conference on the mechanical and physical behaviour of materials under dynamic loading, vol 183

    Article  Google Scholar 

  32. Sakurai T (2008) The latest trends in aluminum alloy sheets for automotive body panels. Mater Process Res Sect 28:22–28

    Google Scholar 

  33. Salaverria MAP (2009) Intensive use of aluminium in car body construction. In: Proceedings of the European automotive congress, Bratislava, vol 12

  34. Schubert E, Zerner DI, Sepold PG (1997) Laser beam joining of material combinations for automotive applications. Laser Mater Process 3097:212–221

    Article  Google Scholar 

  35. Shishkovsky I, Missemer F, Kakovkina N et al (2013) Intermetallics synthesis in the Fe–Al system via layer by laser 3D laser cladding. Crystals 3:517–529

    Article  Google Scholar 

  36. Siqueira RHM, Oliveira AC, Riva R et al (2014) Mechanical and microstructural characterization of laser-welded joints of 6013-T4 aluminum alloy. J Braz Soc Mech Sci Eng 37(1):133–140

    Article  Google Scholar 

  37. Spisak E, Kaskac L (2013) Mechanical joining methods in car body construction. Transf Invácií 28:168–171

    Google Scholar 

  38. Spisak E, Kaskac L (2016) Alternative joining methods in car body production. Int J Eng Sci 5(11):42–46

    Article  Google Scholar 

  39. Sun X, Stephens EV, Khaleel MA et al (2004) Resistance spot welding of aluminum alloy to steel with transition material—from process to performance—part I: experimental study. Weld J 83(6):188–195

    Google Scholar 

  40. Swentek I, Wood JT (2013) Using the lap-shear test to measure polymer composite interfacial strength. In: The 19th international conference on composite materials, Montréal, Canada, pp 1–8

  41. Wang J-B, Nakagawa T, Mukai Y et al (2015) Development of laser processing robot integrated system solution (LAPRISS) for remote laser welding. In: International conference on robotic welding, intelligence and automation, Osaka, Japan, pp 119–131

    Google Scholar 

  42. Zang W, Sun D, Han L et al (2011) Characterization of intermetallic compounds in dissimilar material resistance spot welded joint of high strength steel and aluminum alloy. ISIJ Int 51(11):1870–1877

    Article  Google Scholar 

  43. Zedan MJ, Doos QM (2018) Resistance spot welding of dissimilar alloys 1008 low carbon steel-5052 aluminum alloy. Int J Curr Eng Technol 8(2):266–269

    Article  Google Scholar 

Download references

Acknowledgements

The authors acknowledge Grants 2016/16683-8 and 2017/26428-8 São Paulo Research Foundation (FAPESP) and Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) for a PhD scholarship.

Author information

Authors and Affiliations

  1. Instituto de Estudos Avançados, IEAv/DCTA, São José dos Campos, SP, Brazil

    Isabela Atílio, Vágner Braga, Rafael Humberto Mota de Siqueira, Sheila Medeiros de Carvalho & Milton Sergio Fernandes de Lima

  2. Instituto Tecnológico de Aeronáutica, ITA/DCTA, São José dos Campos, SP, Brazil

    Isabela Atílio, Vágner Braga & Milton Sergio Fernandes de Lima

Authors
  1. Isabela Atílio
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Vágner Braga
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Rafael Humberto Mota de Siqueira
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Sheila Medeiros de Carvalho
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Milton Sergio Fernandes de Lima
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Isabela Atílio.

Additional information

Technical Editor: Lincoln Cardoso Brandao.

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Atílio, I., Braga, V., de Siqueira, R.H.M. et al. Comparing the weldability of AA6013-T4 aluminium alloy on DP600 dual-phase steel with laser welding and resistance spot welding. J Braz. Soc. Mech. Sci. Eng. 42, 71 (2020). https://doi.org/10.1007/s40430-019-2158-0

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s40430-019-2158-0

Keywords

Search

Navigation