Ni-P-nano Al2 O3 composite coatings were deposited by electroless plating, and their microstructures were observed by SEM (scanning electron microscope). The microhardness and the wear resistance of the Ni-P-nano Al2 O3 composite coatings were measured using microhardness tester and block-on-ring tribometer, respectively, and the comparison with those of Ni-P coatings or Ni-P-micro Al2 O3 coating was given. The influences of aging temperature on their hardness and wear resistance were analyzed. The results showed that the nano Al2 O3 particles were distributed uniformly in the Ni-P-Al2 O3 coatings. Among three kinds of Ni-P based coatings, the hardness and wear resistance of Ni-P-nano Al2 O3 coatings were largest, and the maximum values could be obtained at 400 °C. This indicated that the precipitation of nano Al2 O3 particles would improve the hardness and wear resistance of the Ni-P coatings.
Similar content being viewed by others
references
Monir S M, Vaghefi, Saatehi A, et al. Deposition and Properties of Electroless Ni-P-B4 C Composite Coatings [J]. Surface Coatings and Technology, 2003, 168(4): 259.
Pimenav S M, Shafeev G A, Konov V L, et al. Electroless Metallization of Diamond Films [J]. Diamond and Related Materials, 1996, 132(5): 1042.
Song Z, Kishimoto S, Shinya N. Fabrication of Ni-P Alloy Closed Cellular Solid Containing Polymer by the Pulse Current Hot Pressing Technique [J]. Journal of Materials Science, 2003, 38: 4211.
ZHOU Guang-hong, DING Hong-yan. Preparation of Composite Film of Amorphous Ni-P Alloy with Nano-Al2O3 [J]. Transaction of Materials and Heat Treatment, 2004, 25(4): 81 (in Chinese).
Ger Ming-Der, Hwang Bing Joe. Effect of Surfactant on Co-Deposition of PTFE Particles With Electroless Ni-P Coating [J]. Materials Chemistry and Physics, 2002, 76(1): 38.
Balaraju J N, Sankara Naryanan T S N, Seshasrl S K. Electroless Ni-P Composite Coating [J]. Journal of Applied Electrochemistry, 2003, 33: 807.
HUANG Xin-ming, WU Yu-cheng, ZHENG Yu-chun. Effection of Dispersion on the Structure and Properties of Nano Particle Composite Coating [J]. Plating and Finishing, 1999, 21(5): 12 (in Chinese).
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by Jiangsu Natural Science Foundation of China (04KJB430013); Jiangsu Key Laboratory of Friction Wear Opening Foundation
Rights and permissions
About this article
Cite this article
Zhou, Gh., Ding, Hy., Zhou, F. et al. Structure and Mechanical Properties of Ni-P-Nano Al2 O3 Composite Coatings Synthesized by Electroless Plating. J. Iron Steel Res. Int. 15, 65–69 (2008). https://doi.org/10.1016/S1006-706X(08)60014-X
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(08)60014-X