Abstract
The temperature interval ΔT SE of superelasticity in [001]-oriented Co40Ni33Al27 (at. %) single crystals strained by tension and compression has been studied. It is established that ΔT SE in tension amounts to 220 K, and the reversible B2-L10 martensite transformations in loaded samples take place at 590 K. In the samples strained by compression, ΔT SE decreases to 105 K, and the superelasticity is observed up to 420 K.
Similar content being viewed by others
References
K. Oikawa, T. Ota, T. Ohmori, et al., Appl. Phys. Lett. 81, 5201 (2002).
R. D. James and M. Wuttig, Philos. Mag. A 77, 1273 (1998).
Y. I. Chumlyakov, I. V. Kireeva, I. Karaman, et al., Izv. Vyssh. Ucheb. Zaved., Fiz. 47(9), 4 (2004) [Russ. Phys. J. 47, 893 (2004)].
R. F. Hamilton, H. Sehitoglu, C. Efstathiou, et al., Acta Mater. 54, 587 (2006).
R. F. Hamilton, H. Sehitoglu, C. Efstathiou, et al., Scr. Mater. 53, 131 (2005).
H. E. Karaca, I. Karaman, Y. I. Chumlyakov, et al., Scr. Mater. 51, 261 (2004).
K. Otsuka and C. M. Wayman, Shape Memory Materials (Cambridge Univ., Cambridge, 1998).
Y. Liu and S. P. Galvin, Acta Mater. 45, 4431 (1997).
Author information
Authors and Affiliations
Additional information
Original Russian Text © E.Yu. Panchenko, Yu.I. Chumlyakov, A.V. Ovsyannikov, I. Karaman, 2007, published in Pis’ma v Zhurnal Tekhnicheskoĭ Fiziki, 2007, Vol. 33, No. 13, pp. 32–38.
Rights and permissions
About this article
Cite this article
Panchenko, E.Y., Chumlyakov, Y.I., Ovsyannikov, A.V. et al. High-temperature superelasticity during B2-L10 martensite transformations in Co40Ni33Al27 crystals. Tech. Phys. Lett. 33, 556–559 (2007). https://doi.org/10.1134/S106378500707005X
Received:
Issue Date:
DOI: https://doi.org/10.1134/S106378500707005X