Abstract
Two-sided oxidation experiments were recently conducted at 1000-1200°C in flowing steam with samples of sponge-based Zr-1Nb alloy E110. Although the old electrolytic E110 tubing exhibited a high degree of susceptibility to nodular corrosion and experienced breakaway oxidation rates in relatively short time, the new sponge-based E110 has demonstrated steam oxidation behavior comparable to Zircaloy-4. The sponge-based E110 followed the parabolic law, and the derived oxidation rate constant is in good agreement with the Cathcart-Pawel (CP) correlation at 1100-1200°C. For 1000°C oxidation, the weight-gain of sponge-based E110 is much lower than Zircaloy-4. No breakaway oxidation was observed at 1000°C up to 8000 s. Ring compression tests were conducted to evaluate the residual ductility of oxidized samples at room temperature and at 135°C. All sponge-based E110 specimens were still ductile at 135°C after being oxidized up to 20% equivalent cladding reacted at 1000-1200°C. Metallographic examinations were performed on oxidized E110 specimens to correlate material performance with microstructure.
Similar content being viewed by others
References
J. V. Cathcart, R. E. Pawel, R. A. McKee, R. E. Druschel, G. J. Yurek, J. J. Cambell, and S. H. Jury, “Zirconium Metal-Water Oxidation Kinetics: IV. Reaction Rate Studies,” ORNL/NUREG-17, Aug. 1977.
M. C. Billone, Y. Yan, T. Burtseva, and R. Daum, “Cladding Embrittlement during Postulated Loss-of-Coolant Accidents,” NUREG/CR-6967 ANL-07/04 (2008).
Y. Yan, T. A. Burtseva, and M. C. Billone, “Post-quench Ductility Results for North Anna Highburnup 17×17 ZIRLO Cladding with Intermediate Hydrogen Content,” ANL letter report to NRC, April 17, 2009.
Y. Yan, T. Burtseva, and M. Billone, “High Temperature Oxidation Behavior of Zr-1Nb Cladding Alloy E110,” J. Nucl. Mater. 393, 433–448 (2009).
Garde, A. M., Comstok, R. J., Pan, G., Baranwal, R., Hallstadius, L., Cook, T., and Carrera, F., “Advanced Zirconium Alloy for PWR Application,” J. ASTM Intl., Vol. 7, No. 9 doi:10.1520/JAI103030.
Chabretou, V., Hoffmann, P. B., Trapp-Pritsching, S., Garner, G., Barberis, P., Rebeyrolle, V. and Vermoyal, J. J., “Ultra Low Tin Quaternary Alloys PWR Performance-Impact of Tin Content on Corrosion Resistance, Irradiation Growth, and Mechanical Properties,” J. ASTM Intl., Vol. 8, No. 5, doi:10.1520/JAI103013.
L. Yegorova, K. Lioutov, N. Jouravkova, A. Konobeev, V. Smirnov, V. Chesanov, and A. Goryachev, “Experimental Study of Embrittlement of Zr-1%Nb VVER Cladding under LOCA-Relevant Conditions,” NUREG/IA-0211, March 2005.
J. P. Mardon, J. C. Brachet, L. Portier, V. Maillot, T. Forgeron, A. Lesbros, and N. Waeckel, “Influence of Hydrogen Simulating Burn-Up Effects on the Metallurgical and Thermal-Mechanical Behavior of M5™ and Zircaloy-4 Alloys under LOCA Conditions,” ICONE13-50457, 13th Intl. Conf. on Nucl. Eng., Beijing, China, May 16–20, 2005, p. 1–9.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Yan, Y., Garrison, B.E., Smith, T.S. et al. Investigation of High-temperature Oxidation Kinetics and Residual Ductility of Oxidized Samples of Sponge-based E110 Alloy Cladding Tubes. MRS Advances 2, 1203–1208 (2017). https://doi.org/10.1557/adv.2016.641
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2016.641