Abstract
As a consequence of the growing theoretically predictions of 100% spin polarized half– and full–Heusler compounds over the past 6 years, Heusler alloys are among the most promising materials class for future magnetoelectronic and spintronic applications. We have integrated Co2MnSi as a representative of the full–Heusler compound family as one magnetic electrode into technological relevant magnetic tunnel junctions. The resulting tunnel magnetoresistance at 20 K was determined to be 95% corresponding to a Co2MnSi spin polarization of 66% in combination with an AlOx barrier thickness of 1.8 nm. For magnetic tunnel junctions prepared with an initially larger Al layer prior to oxidation the tunnel magnetoresistance at 20 K increases to about 108% associated with a Co2MnSi spin polarization of 72% clearly proving that Co2MnSi is already superior to 3d-based magnetic elements or their alloys. The corresponding room temperature values of the tunnel magnetoresistance are 33% and 41%, respectively. Structural and magnetic properties of the Co2MnSi AlOx – barrier interface have been studied with X-ray diffraction, electron and X-ray absorption spectroscopy and X-ray magnetic circular dichroism and it is shown that the ferromagnetic order of Mn and Co spins at this interface is only induced in optimally annealed Co2MnSi layer. The underlying atomic ordering mechanism responsible for achieving about its theoretical magnetic moment could be assigned to the elimination of Co-Si antisite defects whereas the reduction of Co-Mn antisite defects results in large tunnel magnetoresistance. The presence of a step like tunnel barrier which is already created during plasma oxidation while preparing the AlOx tunnel barrier has been identified as the current limitation to achieve larger tunnel magnetoresistance and hence larger spin polarization and is a direct consequence of the oxygen affinity of the Co2MnSi - Heusler elements Mn and Si.
Preview
Unable to display preview. Download preview PDF.
References
P. Grünberg, R. Schreiber, Y. Pang, M. B. Brodsky, and H. Sowers: Phys. Rev. Lett. 57, 2442 (1986)
M.N. Baibich, J.M. Broto, A. Fert, F. Nguyen Van Dau, F. Petroff, P. Eitenne, G. Creuzet, A. Friederich, and J. Chazelas: Phys. Rev. Lett. 61, 2472 (1988)
M. Julliere: Phys. Lett. 54A, 225 (1975)
J.S. Moodera, L.R. Kinder, T.M. Wong, and R. Meservey: Phys. Rev. Lett. 74, 3273 (1995)
T. Miyazaki and N. Tezuka: J. Magn. Magn. Mater. 139, L231 (1995)
.A. Wolf, D.D. Awschalom, R.A. Buhrman, J.M. Daughton, S. von Molnár, M.L. Roukes, A.Y. Chtchelkanova, and D.M. Treger: Science 294, 1488 (2001)
J.M.D. Coey and C.L. Chien: MRS Bulletin 28, 720 (2003)
C. Palmstrom: MRS Bulletin 28, 725 (2003)
R.A. de Groot. F.M. Mueller, P.G. van Engen, and K.H.J. Buschow: Phys. Rev. Lett. 50, 2024 (1983)
J. Tobola, J. Pierre, S. Kaprzyk, R.V. Skolozdra, and M.A. Kouacou: J. Phys. Condens. Matter 10, 1013 (1998)
J. Tobola and J. Pierre: J. Alloys Comp. 296, 243 (2000)
I. Galanakis, P. H. Dederichs, and N. Papanikolaou: Phys. Rev. B 66, 134428 (2002)
S. Ishida, T. Masaki, S. Fujii, and S. Asano: Physica B 245, 1 (1998)
A. Ayuela, J. Enkovaara, K. Ullakko, and R.M. Nieminen: J. Phys. Condens. Matter 11, 2017 (1999)
A. Deb and Y. Sakurai: J. Phys. Condens. Matter 12, 2997 (2000)
I. Galanakis, P. H. Dederichs, and N. Papanikolaou: Phys. Rev. B 66, 174429 (2002)
J. Nogues and I.K. Schuller: J. Magn. Magn. Mater. 192, 203 (1999)
A.E. Berkowitz and K. Takano: J. Magn. Magn. Mater. 200, 552 (1999)
C.T. Tanaka, J. Nowak, and J.S. Moodera: J. Appl. Phys. 86, 6239 (1999)
K. Inomata, S. Okamura, R. Goto, and N. Tezuka: Jpn. J. Appl. Phys. 42, L419 (2003)
A. Thomas, Ph.D. thesis, Department of Physics, University of Bielefeld (2004)
P.J.~Brown, K.U.~Neumann, P.J.~Webster, and K.R.A.~Ziebeck: J. Phys. Condens. Matter 12, 1827 (2000)
R. Meservey, D. Pereskevopoulus, and P.M. Tedrow: Phys. Rev. Lett. 37, 858 (1976)
R.C. O'Handley. In: Modern Magnetic Materials, (John Wiley & Sons, New York 2000) p. 100
L.J. Singh, Z.H. Barber, Y. Miyoshi, Y. Bugoslavsky, W.R. Branford, and L.F. Cohen: unpublished, preprint arXiv:cond-mat/031116
S. Kämmerer, A. Thomas, A. Hütten, and G. Reiss: Appl. Phys. Lett. 85, 79 (2004)
A. Hütten, S. Kämmerer, J. Schmalhorst, A. Thomas, and G. Reiss: Phys. Stat. Sol. (a), ) 201, 3271 (2004)
S. Kämmerer, S. Heitmann, D. Meyners, D. Sudfeld, A. Thomas, A. Hütten, and G. Reiss: J. Appl. Phys. 93, 7945 (2003)
A. Thomas, H. Brückl, M.D. Sacher, J. Schmalhorst, and G. Reiss: J. Vac. Sci. Technol. B 21, 2120 (2003)
J.C. Slonczewski: Phys. Rev. B 39, 6995 (1989)
A. Hütten, T. Hempel, S. Heitmann, and G. Reiss: Phys. Stat. Sol. (a) 189, 327 (2002)
E.C. Stoner and E.P. Wohlfarth: Phil. Trans. R. Soc. Lond. A 240, 599 (1948)
R.M. Bozorth. In: Ferromagnetism (IEEE Press, New York 1978) p. 194
Lange's handbook of chemistry, ed by J. Dean, (McGraw-Hill Book Company, New York 1973)
J. Schmalhorst, S. Kämmerer, M. Sacher, G. Reiss, A. Hütten, and A. Scholl: Phys. Rev. B 70, 024426 (2004)
S. Kämmerer: Ph.D. thesis, Department of Physics, University of Bielefeld (2004)
W.F. Brinkman, R.C. Dynes, and J.M. Rowell: J. Appl. Phys. 41, 1915 (1970)
S. Picozzi, A. Continenza, and A.J. Freeman: Phys. Rev. B 69, 094423 (2004)
Reference database, International Centre for Diffraction Data (1999)
P.J. Webster: Contemp. Phys. 10, 559 (1969)
Author information
Authors and Affiliations
Editor information
Rights and permissions
About this chapter
Cite this chapter
Hütten, A., Kämmerer, S., Schmalhorst, J., Reiss, G. Heusler Alloyed Electrodes Integrated in Magnetic Tunnel-Junctions. In: Galanakis, I., Dederichs, P. (eds) Half-metallic Alloys. Lecture Notes in Physics, vol 676. Springer, Berlin, Heidelberg. https://doi.org/10.1007/11506256_8
Download citation
DOI: https://doi.org/10.1007/11506256_8
Published:
Publisher Name: Springer, Berlin, Heidelberg
Print ISBN: 978-3-540-27719-4
Online ISBN: 978-3-540-31517-9
eBook Packages: Physics and AstronomyPhysics and Astronomy (R0)