Abstract
The fracture properties of two commercial epoxide resins both unfilled and filled with varying volume fraction of silica, alumina and dolomite particles have been investigated. The variation in the stress intensity factor with the crack velocity was measured using the double torsion test technique. In order to examine the influence of the resin-filler adhesion on the fracture toughness, alumina particles were treated with three silane compounds. In addition the yield stresses and the flexural strengths were measured. In an attempt to si-mulate resin-filler interactions and to measure the fracture energy for interfacial separation a scarf joint was used with a bond angle of 45 °. This geometry produces a mixture of mode I and mode II loading. The combined mode strain energy release rate (G(I,II)c) was determined.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
D.C. Phillips and B. Harris, in “Polymer Engineering Composites”, M.O.W. Richardson Editor, Ch. 2, Appliqd Science, London 1977.
K.L. Mittal, Solid State Technol. ( May 1979 ) 89.
K.L. Trachte and A.T. DiBenedetto, Int. J. Polym. Mater., 1, 75 (1971).
R.W. Davidge and G. Tappin, J. Mater. Sci., 3, 165 (1968).
C. Tourenq and F. Gragger, Naturstein Ind., 11, 19 (1965).
S.M. Wiederhorn, J. Amer. Ceram. Sac., 52, 99 (1969).
A.G. Evans, J. Mater. Sci., 7, 1137 (1971).
H.G. Tattersall and G. Tappin, J. Mater. Sci., 1, 296 (1966).
B.J. Pletka, E.R. Fuller and B.G. Loepke, in “Fracture Mechanics Applied to Brittle Materials”, STP No. 678, p. 3, 19, ASTM, Philadelphia, PA, 1979.
B. Stalder and H.H. Kausch, J. Mater, Sci., 17, 2481 (1982).
P. Leevers, J. Mater, Sci., 17, 2469 (1982).
B. Stalder, Ph. Béguelin and H.H. Kausch, Int. J. Fract., in press (1982).
J.G. Williams and H. Ford, J. Mech. Eng. Sci., 6, 7 (1964).
G.C. Trantina, J. Comp. Mater., 6, 371 (1972).
W.D. Bascom, C.O. Timmons and R.L. Jones, J. Mater. Sci., 10, 1037 (1975).
W.D. Bascom and J. Oroshnik, J. Mater. Sci., 13, 1411 (1978).
L.J. Broutman and S. Sahu, Mater. Eng. Sci., 8, 98 (1971).
J.C. Hammond and D.C. Quayle, Second Int. Conf. on Deformation, Yield and Fracture of Polymers, P.R.I., March 1973, Cambridge, UK
A.C. Moloney, H.H. Kausch and H.R. Stieger, manuscript in preparation (1983).
S. Kunz-Douglass, P.W.R. Beaumont and M.F. Ashby, J. Mater. Sci., 15, 1109 (1980).
F.F. Lange, Phil. Mag., 22, 983 (1970).
F.F. Lange, J. Amer. Ceram. Soc., 54, 614 (1971).
A.C. Moloney, H.H. Kausch and H.R. Stieger, J. Mater. Sci., 18, 208 (1983).
J.A. Manson and L.H. Sperling, “Polymer Blends and Composites”, Plenum Press, New York, 1976.
O. Ishai and L.J. Cohen, Int. J. Mech. Sci., 9, 539 (1967).
R.J. Young and P.W.R. Beaumont, J. Mater. Sci., 10, 1343 (1975) and 12, 684 (1977).
A.G. Evans, Phil. Mag., 26 /6, 1327 (1972).
D.J. Green, P.S. Nicholson and J.D. Embery, J. Mater. Sci., 14, 1657 (1979).
F.F. Lange and K.C. Radford, J. Mater. Sci., 6, 1197 (1971).
A.J. Kinloch, J. Mater. Sci., 15, 2141 (1980).
R.A. Gledhill, A.J. Kinloch, S. Yamini and R.J. Young, Polymer, 19, 574 (1978).
A.K. Saxena, Fibre Sci. Technol., 12, 111 (1979).
D.R. Mulville, P.W. Mast and R.N. Vaishnav, J. Eng. Mater. Technol., 100, 27 (1978).
D.R. Mulville and R.N. Vaishnav, J. Adhesion, 7, 215 (1975).
W.D. Bascom, R.L. Cottington and C.O. Timmons, J. Appl. Polym. Sci. Appl. Polym. Symp., 32, 165 (1977).
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1984 Plenum Press, New York
About this chapter
Cite this chapter
Moloney, A.C., Kausch, H.H., Stieger, H.R. (1984). Interfacial Properties of Filled Epoxide Resins. In: Mittal, K.L. (eds) Adhesive Joints. Springer, Boston, MA. https://doi.org/10.1007/978-1-4613-2749-3_51
Download citation
DOI: https://doi.org/10.1007/978-1-4613-2749-3_51
Publisher Name: Springer, Boston, MA
Print ISBN: 978-1-4612-9702-4
Online ISBN: 978-1-4613-2749-3
eBook Packages: Springer Book Archive