Abstract
Based on three-dimensional processing maps and numerical simulation, a demo flat bottom cylindrical part (with outer diameter of 235 mm, wall thickness of 34 mm, and height of 255 mm) of high strength Mg-Gd-Y magnesium alloy was hot backward extruded by adding an outer flange to increase the overall deformation amount and strain uniformity. Firstly, on the basis of dynamic material model and Murty instability criterion, isothermal compression stress-strain curves of cast-homogenized Mg-8Gd-3Y alloy were used to construct the processing maps. The processing maps show that the formable domain is relatively narrow: at lower strain rates ranging from 0.001 to 0.006 s−1, and the suitable temperature is from 350 to 450 °C; and at higher strain rates ranging from 0.006 to 0.1 s−1, and the temperature is from 410 to 450 °C. Then, the processing maps were integrated into a finite element software to simulate the forming process of cylindrical parts, and the influences of deformation temperature and velocity on the power dissipation efficiencies of different positions of flanged cylindrical parts were mainly discussed. The simulation results indicate that the average strain of flanged cylindrical parts reaches 30.07% and is larger than that of unflanged cylindrical parts, and the standard deviation of the strain of flanged cylindrical parts is 19.35% and less than that of unflanged cylindrical parts. The optimal process parameters corresponding to the maximum power dissipation efficiency are the temperature of 430 °C and velocity of 1 mm/s. Finally, under the optimal forming condition, the hot backward extrusion experiments of flanged cylindrical parts were conducted. The experimental results exhibit that the flanged cylindrical parts could be properly formed with good surface quality, and have relatively uniform microstructures and mechanical properties. The difference of tensile strength between the bottom and cylindrical body is less than 5 MPa, and the hardness difference is less than 1.6 HV.
Similar content being viewed by others
References
Xie ZY, Tian Y, Li Q, Zhou JC, Meng Y (2019) Effects of forming parameters on microstructure and mechanical properties of a cup-shaped Mg–8.20Gd–4.48Y–3.34Zn–0.36Zr alloy sample manufactured by thixoforming. Int J Adv Manuf Technol 101:1807–1819
Alizadeh R, Mahmudi R, Ruano OA, Ngan AHW (2017) Constitutive analysis and hot deformation behavior of fine-grained Mg-Gd-Y-Zr alloys. Metall Mater Trans A 48A:5699–5709
Zeng J, Wei XX, Dong S, Wang FH, Jin L, Dong J (2020) 3D processing maps of cast Mg-8Gd-3Y alloy at high strain rates and their application in plane strain forging. Int J Adv Manuf Technol 106:133–141
Xia XS, Xiao L, Chen Q, Li H, Tan YJ (2018) Hot forging process design, microstructure, and mechanical properties of cast Mg–Zn–Y–Zr magnesium alloy tank cover. Int J Adv Manuf Technol 94:4199–4208
Yuan L, Zhao Z, Shi WC, Xu FC, Shan DB (2015) Isothermal forming of large-size AZ80A magnesium alloy forging with high mechanical properties. Int J Adv Manuf Technol 78:2037–2047
Liu B, Zhang ZY, Jin L, Gao JL, Dong J (2016) Forgeability, microstructure and mechanical properties of a free-forged Mg–8Gd–3Y–0.4Zr alloy. Mater Sci Eng A 650:233–239
Liu J, Cui ZS (2009) Hot forging process design and parameters determination of magnesium alloy AZ31B spur bevel gear. J Mater Process Technol 209:5871–5880
Liu J, Li JQ, Cui ZS, Qu HA, Ruan LQ (2013) Material driven workability simulation by FEM including 3D processing maps for magnesium alloy. Trans Nonferrous Metals Soc China 23:3011–3019
Sun CY, Xiang Y, Liu G, Zuo X, Wang MQ, Zhang QD (2017) Extrusion limit diagram of IN 690 super-alloy tube based on hot processing map. Int J Adv Manuf Technol 89:3419–3428
Lu J, Song Y, Hua L, Zheng KL, Dai DG (2018) Thermal deformation behavior and processing maps of 7075 aluminum alloy sheet based on isothermal uniaxial tensile tests. J Alloys Compd 767:856–869
Li PW, Li HZ, Huang L, Liang XP, Zhu ZX (2017) Characterization of hot deformation behavior of AA2014 forging aluminum alloy using processing map. Trans Nonferrous Metals Soc China 27:1677–1688
Sun Y, Feng XY, Hu LX, Zhang H, Zhang HZ (2018) Characterization on hot deformation behavior of Ti-22Al-25Nb alloy using a combination of 3D processing maps and finite element simulation method. J Alloys Compd 753:256–271
Du ZH, Jiang SS, Zhang KF (2015) The hot deformation behavior and processing map of Ti–47.5Al–Cr–V alloy. Mater Des 86:464–476
Li JQ, Liu J, Cui ZS (2014) Characterization of hot deformation behavior of extruded ZK60 magnesium alloy using 3D processing maps. Mater Des 56:889–897
Shang X, Zhou J, Wang X, Luo Y (2015) Optimizing and identifying the process parameters of AZ31 magnesium alloy in hot compression on the base of processing maps. J Alloys Compd 629:155–161
Lv BJ, Peng J, Shi DW, Tang AT, Pan FS (2013) Constitutive modeling of dynamic recrystallization kinetics and processing maps of Mg–2.0Zn–0.3Zr alloy based on true stress–strain curves. Mater Sci Eng A 560:727–733
Xu C, Pan JP, Nakata T, Qiao XG, Chi YQ, Zheng MY, Kamado S (2017) Hot compression deformation behavior of Mg-9Gd-2.9Y-1.9Zn-0.4Zr-0.2Ca (wt%) alloy. Mater Charact 124:40–49
Xu WC, Jin XZ, Shan DB, Chai BX (2017) Study on the effect of solution treatment on hot deformation behavior and workability of Mg-7Gd-5Y-0.6Zn-0.8Zr magnesium alloy. J Alloys Compd 720:309–323
Azimi M, Mirjavadi SS, Salandari-Rabori A (2018) Effect of temperature on microstructural evolution and subsequent enhancement of mechanical properties in a backward extruded magnesium alloy. Int J Adv Manuf Technol 95:3155–3166
Chalay-Amoly A, Zarei-Hanzaki A, Changizian P, Fatemi-Varzaneh SM, Maghsoudi MH (2013) An investigation into the microstructure/strain pattern relationship in backward extruded AZ91 magnesium alloy. Mater Des 47:820–827
Zhang XY, Mei RB, Li PP, Bao L, Zhang J, Zhou YZ (2016) Numerical analysis of deformation of AZ31 magnesium alloy in backward extrusion with counter pressure. Mater Sci Forum 861:216–221
Fatemi-Varzaneh SM, Zarei-Hanzaki A, Naderi M, Roostaei AA (2010) Deformation homogeneity in accumulative back extrusion processing of AZ31 magnesium alloy. J Alloys Compd 507:207–214
Zeng J, Wang FH, Wei XX, Dong S, Zhang ZY, Dong J (2020) A new constitutive model for thermal deformation of magnesium alloys. Metall Mater Trans A 51A:497–512
Ding XF, Zhao FQ, Shuang YH, Ma LF, Chu ZB, Zhao CJ (2020) Characterization of hot deformation behavior of as-extruded AZ31 alloy through kinetic analysis and processing maps. J Mater Process Technol 276:116325
Luo J, Li MQ, Yu WX, Li H (2009) Effect of the strain on processing maps of titanium alloys in isothermal compression. Mater Sci Eng A 504:90–98
Samantaray D, Mandal S, Bhaduri AK (2011) Characterization of deformation instability in modified 9Cr–1Mo steel during thermo-mechanical processing. Mater Des 32:716–722
Murty SVSN, Rao BN (1998) On the development of instability criteria during hotworking withreference to IN 718. Mater Sci Eng A 254:76–82
Ma X, Zeng WD, Xu B, Sun Y, Xue C, Han YF (2012) Characterization of the hot deformation behavior of a Ti-22Al-25Nb alloy using processing maps based on the Murty criterion. Intermetallics 20:1–7
Güzel A, Jäger A, Parvizian F, Lambers HG, Tekkaya AE, Svendsen B, Maier HJ (2012) A new method for determining dynamic grain structure evolution during hot aluminum extrusion. J Mater Process Technol 212:323–330
Funding
This work was financially supported by the National Key Research and Development Program of China (Grant No. 2016YFB0301103), the National Natural Science Foundation of China (Grant No. 51701117 and Grant No. 51601112), and the Fundamental Research Funds for the Central Universities of China (Grant No. PA2019GDPK0048).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Zeng, J., Wang, F., Dong, S. et al. Optimization of hot backward extrusion process parameters for flat bottom cylindrical parts of Mg-8Gd-3Y alloy based on 3D processing maps. Int J Adv Manuf Technol 108, 2149–2164 (2020). https://doi.org/10.1007/s00170-020-05516-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-020-05516-2