Abstract
The Bi(Pb)-2223 superconductor has been prepared via coprecipitation (COP) method from solutions of metal acetates and 2-propanol solution of oxalic acid at low temperature (0–2 °C). The metal oxalates powder was subjected to precalcination of 12 h at 730 °C, followed by 24 h calcination at 845 °C. The pelletized powder was sintered for 24, 48 and 100 h at 850 °C. The dominance of high-T C phase was observed for all samples as evidenced in the single step transition of (R–T) curves. The T C(R = 0) for samples sintered at 24, 48 and 100 h were 102, 102 and 104 K, respectively. XRD data showed the tetragonal structure for all samples followed by the enhancement of the 2223 phase as sintering time increased. Ac magnetic susceptibility measurements showed the improvement of the grain connectivity as sintering time increased. SEM micrographs showed large flaky grains of ∼7 μm in size and randomly distributed, which belong to 2223 phase. The degree of grains alignment increased as the sintering time increased.
Similar content being viewed by others
References
Rouessac V, Wang J, Provost J, Desgardin G (1996) J Mat Sci 31:3387
Chin TS, Huang TW, Lin WT, Wa NC, Chou YH, Wu TC, Wu PT, Yen HH (1988) Mat Res Soc Symo Proc 99:261
Ciontea L, Boffa V, Petrisor T, Bruzzese R, Perte E, Alvani C (1996) Physica C 257:304
Mao C, Zhou L, Sun X, Wu X (1997) Physica C 281:35
Monica P, Alina T, Liliana P, Dragan N, Maria Z (1998) J Eur Ceram Soc 18:1265
Rama Rao GV, Swaminathan K, Sreedharan OM, Venkadesan S, Mannan SL (1998) J Mater Sci 33:1511
Halim SA, Khawaldeh SA, Mohamed SB, Azhan H (1999) Mat Chem & Phys 61:251
Halim SA, Khawaldeh SA, Azhan H, Mohamed SB (2000) J Mat Sci 35:3043
Prker SP (1987) Solid state physics source book. McGraw-Hill Book Company, New York, p 151
Badica P, Aldica G, Bunescu MC, Nemyarovsky AV (2000) J Mater Sci Lett 19:561
Hsueh YW, Chang SC, Liu RS, Woodall L, Gerards M (2001) Mater Res Bull 36:1653
Driessche IV, Buekenhoudt A, Konstantinov K, Bruneel E, Hoste S (1996) Anal Appl Supercond 4:185
Matsushita T, Suzuki A, Kishida T, Okuda M, Naito H (1994) Supercond Sci Technol 7:222
Emmen JH, Barbers VAM, De Jonge WJ, Steen CVD, Dalderop JHJ, Geppart PMA, Kopinga K (1989) J Less Common Metals 151:63
Ambegaokar V, Baratoff A (1963) Phys Rev Lett 10:486
Azhan H (1999) Effect of Sn doping and heat treatment on Bi–Sr–Ca–Cu–O superconducting ceramics. Ph.D Thesis at Physics Department, Faculty of Science, Universiti Putra Malaysia, pp 218–221
Acknowledgements
The financial support of the IRPA Grant vote: 4-07-05-026 (High Temperature Superconductors) from the Ministry of Science, Technology and Innovation Malaysia is gratefully acknowledged. The authors would like to express their gratitude to electron microscopy unit at Institute of Biosciences (UPM) for rendering the facility of JEOL 6400 scanning electron microscopy (SEM).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hamadneh, I., Halim, S.A. & Lee, C.K. Characterization of Bi1.6Pb0.4Sr2Ca2Cu3Oy ceramic superconductor prepared via coprecipitation method at different sintering time . J Mater Sci 41, 5526–5530 (2006). https://doi.org/10.1007/s10853-006-0277-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0277-3